BASF Ultramid® B3GK24 BK 00564 10/20% Glass/Glass Bead Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled , Nylon 6, Glass Bead Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® B3GK24 BK 00564 10/20% Glass/Glass Bead Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: combined 10% glass-fiber and 20% glass-bead reinforced injection-molding grade for technical articles of very good dimensional stability, for instance, vehicle ash tray housings and electronic housings.Information provided by BASF

Physical Properties	Metric	English	Comments
Bulk Density	0.500 - 0.800 g/cc	0.0181 - 0.0289 lb/in³
Density	1.34 g/cc	0.0484 lb/in³	ISO 1183
Water Absorption	6.3 - 6.9 %	6.3 - 6.9 %	Saturation; ISO 62
Moisture Absorption at Equilibrium	1.9 - 2.3 %	1.9 - 2.3 %	23°C; 50% RH; ISO 62
Viscosity Measurement	140	140	ISO 307
Linear Mold Shrinkage	0.0050 cm/cm	0.0050 in/in	restricted
Melt Flow	93.8 g/10 min @Load 5.00 kg, Temperature 275 °C	93.8 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	110 MPa	16000 psi	50 mm/min; ISO 527-1/-2
Elongation at Yield	3.5 %	3.5 %	50 mm/min; ISO 527-1/-2
Modulus of Elasticity	6.00 GPa	870 ksi	ISO 527-1/-2
Flexural Strength	130 MPa	18900 psi	at max force; ISO 178
	175 MPa	25400 psi	ISO 178
Flexural Modulus	5.00 GPa	725 ksi	ISO 178
Izod Impact, Notched (ISO)	5.00 kJ/m² @Temperature 23.0 °C	2.38 ft-lb/in² @Temperature 73.4 °F	ISO 180/A
Charpy Impact Unnotched	3.90 J/cm² @Temperature -30.0 °C	18.6 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	4.00 J/cm² @Temperature 23.0 °C	19.0 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.450 J/cm² @Temperature -30.0 °C	2.14 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.500 J/cm² @Temperature 23.0 °C	2.38 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	35.0 - 40.0 µm/m-°C @Temperature 23.0 - 80.0 °C	19.4 - 22.2 µin/in-°F @Temperature 73.4 - 176 °F	DIN 11359-1/-2
Specific Heat Capacity	1.40 J/g-°C	0.335 BTU/lb-°F
Thermal Conductivity	0.340 W/m-K	2.36 BTU-in/hr-ft²-°F	DIN 52612
Melting Point	220 °C	428 °F	DIN 53765
Maximum Service Temperature, Air	100 °C	212 °F	for 50% loss of tensile strength after 20000hr
	200 °C	392 °F
Deflection Temperature at 0.46 MPa (66 psi)	200 °C	392 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	150 °C	302 °F	ISO 75-1/-2
Decomposition Temperature	>= 300 °C	>= 572 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	3.9 @Frequency 1.00 Hz	3.9 @Frequency 1.00 Hz	IEC 60250
Dissipation Factor	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	425 V	425 V	Test solution A; IEC 60112

Processing Properties	Metric	English	Comments
Processing Temperature	80.0 °C	176 °F	Hopper Throat
Zone 1	260 °C	500 °F	Feed Zone
Zone 2	270 °C	518 °F	Compression
Zone 3	280 °C	536 °F	Metering-zone
Zone 4	280 °C	536 °F	Nozzle
Melt Temperature	270 - 290 °C	518 - 554 °F	Injection-molding/Extrusion
	280 °C	536 °F	Optimal
Mold Temperature	80.0 °C	176 °F	Optimal
	80.0 - 90.0 °C	176 - 194 °F	Injection-molding
Drying Temperature	80.0 °C	176 °F
Dry Time	4 hour	4 hour
Moisture Content	0.030 - 0.060 %	0.030 - 0.060 %	Optimal
	<= 0.15 %	<= 0.15 %

Descriptive Properties	Value	Comments
Color	BK 00564
Commercial Status	Europe
Ignition Temperature	>400°C	ASTM D129
Peripheral screw speed	< 0.3 m/s