Schwartz Technical Plastics OPTAMID® Cast Polyamide 6, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | OPTAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics OPTAMID® Cast Polyamide 6, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: deflection rope sheaves for elevatorsInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | DIN 53473 |
| Water Absorption at Saturation | 7.0 % @Temperature 20.0 °C |
7.0 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 150 MPa | 21800 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO-DIS 527 |
| Creep Strength | 20.0 MPa | 2900 psi | 1% elongation, 1000 h; DIN 53444 |
| 22.0 MPa | 3190 psi | 2% elongation, 1000 h; DIN 53444 | |
| Tensile Modulus | 3.50 GPa | 508 ksi | DIN 53457 |
| Flexural Strength | 130 MPa | 18900 psi | DIN 54352 |
| Flexural Modulus | 3.10 GPa | 450 ksi | DIN 53457 |
| Izod Impact, Notched (ISO) | >= 3.70 kJ/m² | >= 1.76 ft-lb/in² | DIN 53453 |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.040 | 0.040 | With lubrication |
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | >= 0.25 | >= 0.25 | ISO-DIS 527 |
| K Factor (Wear Factor) | 9.00e-11 | 9.00e-11 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 - 80.0 µm/m-°C @Temperature 20.0 - 100 °C |
38.9 - 44.4 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous |
| 180 °C | 356 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | V-notch; ISO R 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | V-notch; ISO R 75 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.7 | 3.7 | DIN 53483 |
| Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.030 | 0.030 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA3c | DIN 53480 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 2103-22 CR-SX-HT Fiberglass Reinforced Thermoset BMC
- DuPont™ Clysar® ABL Polyolefin Shrink Packaging Film, 75 Gauge (discontinued **)
- NOVA Chemicals Novapol® PF-Y821-D Butene LLDPE Film Resin (discontinued **)
- LG Chemical Lupoy 1200-03 Polycarbonate Resin
- Samsung Cheil Industries Infino® WP-1098 PC/ABS, Unreinforced
- A. Schulman PP 1248-01 Polypropylene High-Flow Homopolymer Polypropylene
- A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy
- Eagle Brass 770 Nickel Silver 18%, 1/4 Hard
- DuPont™ Kapton® CR Polyimide Film
- Chase Plastics CP Pryme® PCA300 General Purpose Polycarbonate/ABS Alloy (Utility Grade)
Copyright © lookpolymers.com All Rights Reserved