SABIC Innovative Plastics Valox® VX5011 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® VX5011 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX VX5011 is a 10% glass fibre reinforced PBT+PC blend with low warpage characteristics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ASTM D229 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Viscosity | 145000 cP | 145000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0080 cm/cm | 0.0030 - 0.0080 in/in | on Tensile Bar; SABIC Method |
| 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0090 cm/cm | 0.0050 - 0.0090 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 18 g/10 min @Load 3.80 kg, Temperature 200 °C |
18 g/10 min @Load 8.38 lb, Temperature 392 °F |
ASTM D1238 |
| 85 g/10 min @Load 5.00 kg, Temperature 265 °C |
85 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 | |
| 85 g/10 min @Load 5.00 kg, Temperature 266 °C |
85 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 | |
| Melt Index of Compound | 18 g/10 min @Load 2.16 kg, Temperature 250 °C |
18 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 50 g/10 min @Load 5.00 kg, Temperature 250 °C |
50 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 75 g/10 min @Load 5.00 kg, Temperature 265 °C |
75 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ISO 2039-2 |
| Hardness, H358/30 | 165 MPa | 23900 psi | ISO 2039-1 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| 5.0 % | 5.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.60 GPa | 667 ksi | 5 mm/min; ASTM D638 |
| 4.70 GPa | 682 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 130 MPa | 18900 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 126 MPa | 18300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 140 MPa | 20300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.60 GPa | 522 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.00 GPa | 580 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.470 J/cm | 0.881 ft-lb/in | ASTM D256 |
| 0.470 J/cm @Temperature 0.000 °C |
0.881 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.470 J/cm @Temperature -30.0 °C |
0.881 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 4.75 J/cm | 8.90 ft-lb/in | ASTM D4812 |
| 4.65 J/cm @Temperature -30.0 °C |
8.71 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature 0.000 °C |
2.38 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/2C |
| 4.00 J/cm² | 19.0 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/2C | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Dart Drop, Total Energy | 37.0 J @Temperature 23.0 °C |
27.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 54 | 54 | CS-17, 1 kg; SABIC Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 50.0 - 60.0 Hz |
3.0 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
| 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| 29.0 kV/mm @Thickness 0.800 mm |
737 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| 29.0 kV/mm @Thickness 0.800 mm |
737 kV/in @Thickness 0.0315 in |
in oil; ASTM D149 | |
| Dissipation Factor | 0.0090 @Frequency 50.0 - 60.0 Hz |
0.0090 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.014 @Frequency 1.00e+6 Hz |
0.014 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| 0.014 @Frequency 1.00e+6 Hz |
0.014 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.016 @Frequency 100 Hz |
0.016 @Frequency 100 Hz |
IEC 60250 | |
| Comparative Tracking Index | >= 100 V | >= 100 V | IEC 60112 |
Users viewing this material also viewed the following:
- ExxonMobil Escorene® LD-102 LDPE Drawdown Resin, 1.25 mil Film (discontinued **)
- NOVA Chemicals Sclair® 58A/58A-DE3 HDPE Blow Molding Resin
- Lushan PR-2A Maleic Anhydride Grafted Polypropylene
- SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer (Asia Pacific)
- SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP DF006 PC
- A. Schulman POLYFORT™ PP 7001
- Ametek P316L P/M Stainless Steel, Sintered from 6.25 g/cc Green Density
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.0 PHR MBTS