Polyram PlusTek RA325J5 Nylon 6.6, 25% Glass beads and Glass Fiber, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA325J5 Nylon 6.6, 25% Glass beads and Glass Fiber, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
25% glass beads and glass fiber reinforced, flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | DIN 53479 |
| Water Absorption | 6.0 % | 6.0 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ASTM-D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM-D638 |
| Tensile Modulus | 5.00 GPa | 725 ksi | ASTM-D790 |
| Flexural Strength | 130 MPa | 18900 psi | ASTM D790 |
| Flexural Modulus | 3.70 GPa | 537 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.400 J/cm @Temperature 23.0 °C |
0.749 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- ND Industries 230 Structural Adhesive
- Lehmann & Voss LUVOCOM® 19-7276 Polyamide 46, with carbon fiber and PTFE
- Mitsubishi Xantar® SF 2230 Polycarbonate-30% Glass Reinforced
- PlastxWorld DAICEL STYROL® GH10 HIPS
- American Elements Carbon Nanoparticles
- Dow Corning SYL-OFF® SL 7688 RELEASE COATING
- A. Schulman ComAlloy Comtuf® 523 Polycarbonate/Styrenic Alloy
- 3M 8891 Bond Breaker Tape
- Henkel Hysol EA 9689 Film Adhesive
- Lanxess Pocan® KU 2-7209 Z 901510 PBT, 15% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved