- Polymer Property : Flexural Strength = 115 MPa
Polymer Property : Flexural Strength = 115 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 115 MPa | 16700 psi | STN EN ISO 178 |
| Plastcom SLOVAMID 6 OB Polyamide 6, Optically Brightened FeaturesPA 6 for injection moulding, optical brightened, for mouldings with high surface brightness, with increased toughness and tensile modulus in comparison with the basic type. The microcrystal.. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Nilit FRIANYL A63 GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | 115 MPa | 16700 psi | |
| Plastcom SLOVASTER® B1 GF 10 MI PBT, 10% glass fibre Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
| Flexural Strength | <= 115 MPa | <= 16700 psi | ISO 178 |
| Polykemi AB POLYfill PPH GF8030 PD1 VT2 PP, Glass Fiber-Reinforced, Chemically Coupled Heat Stabilized Information provided by Polykemi AB |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Nilit FRIANYL B63 FK 1010 Nylon 6 for injection molding, 10% glass fiber and 10% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | 115 MPa | 16700 psi | |
| Lehmann & Voss LUVOCOM® 1-7985 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Emergency running property.Improved heat resistance.Control disks, cams, sliding elements and o.. |
|||
| Flexural Strength | 115 MPa | 16700 psi | |
| Lehmann & Voss LUVOCOM® 50-7224/V0 Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Reduced moment of inertia compared with metal parts.Improved f.. |
|||
| Flexural Strength | 115 MPa | 16700 psi | |
| Lehmann & Voss LUVOCOM® 80-7626 Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricit.. |
|||
| Flexural Strength | 115 MPa | 16700 psi | 1.5 mm/min; ISO 178:2001 |
| Global EPP PA 6C MOLY Cast Polyamide 6 + MoS2 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Kuraray Genestarâ„¢ N1000A-M41 Nylon Standard unreinforced injection grade. Main features:Low water absorptionChemical ResistanceExamples of application are:Friction and wear applicationGear and Wheel |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Lucite International Diakon® CLH952 Acrylic Polymer Information provided by Lucite International |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Lucite International Diakon® CLH952L Acrylic Polymer Information provided by Lucite International |
|||
| Flexural Strength | 115 MPa | 16700 psi | |
| Lehmann & Voss LUVOCOM® 1105/TF/20/NAT PEEK, with PTFE Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Solvay TECHNYL® C 216 PA6, DRY Description: Unreinforced polyamide PA6, standard nucleation for fast cycling, for injection molding.Available in: Asia PacificProduct Applications: This grade has a high fluidity and good mould rel.. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Solvay Technyl® C206F Unfilled, Fast Cycle Nylon 6 Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 |
| Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA), 15% Glass Fiber (Conditioned) Amodel® AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin.. |
|||
| Flexural Strength | 115 MPa | 16700 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® 4012 PBT (Europe-Africa-Middle East) VALOX 4012 is a 10% high strength glass fibre reinforced PBT injection moulding resin with improved mechanical properties. Applications: connectors. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 |
| Techmer ES HiFill® PA6 E2 Availability: North AmericaForms: PelletsProcessing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Strength | 115 MPa | 16700 psi | 2mm/min; ISO 178 |
| Teijin Multilon DN-1520B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 20 % filler. Improved stiffness and high fluidity realizes a thin wall.. |
|||
| Flexural Strength | 115 MPa | 16700 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK500 PC+ABS LNP* Thermocomp* Lexan_JK500 compound is a 10% GR, ECO conforming FR, PC+ABS for thinwall molding applications. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 |
| A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6 Information provided by A. Schulman. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178-93 |
| Wellman Wellamid® GS1684-WBK1 25% Glass Sphere Filled Nylon 66 Description: Glass Sphere Filled Nylon 66Information provided by Wellman. |
|||
| Flexural Strength | 115 MPa | 16700 psi | cond; ISO 178 |
| DSM Novamid® 1013GH15 1 NA/BK37 PA6-GF15 15% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
| Flexural Strength | 115 MPa | 16700 psi | dry; ISO 178 |
| DSM Novamid® 3010SR NAT PA66 Easy Molding Grade |
|||
| Flexural Strength | 115 MPa | 16700 psi | cond; ISO 178 |
| DSM EcoPaXX® Q-HGM24 PA410-(GF+MD)30 10% Glass Reinforced, 20% Mineral Reinforced, Heat Stabilized |
|||
| Flexural Strength | 115 MPa | 16700 psi | 2mm/min; ISO 178 |
| Teijin Panlite® G-3410H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin Reinforced with 10 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPreci.. |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Styrolution Luran® 348 Q Crystal Clear Transparent 77850 SAN Description: Highly transparent grade with low natural color.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Styrolution Luran® 348 Q Transparent SAN Description: Highly transparent grade with light natural color.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS |
|||