Kuraray Genestarâ„¢ N1000A-M41 Nylon
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestarâ„¢ N1000A-M41 Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard unreinforced injection grade. Main features:Low water absorptionChemical ResistanceExamples of application are:Friction and wear applicationGear and Wheel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | |
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 0.25 % | 0.25 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527-1/-2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 |
| Tensile Modulus | 2.72 GPa | 395 ksi | ISO 527-1/-2 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Coefficient of Friction | 0.45 | 0.45 | ISO JIS K7218-A |
| K Factor (Wear Factor) | 200 | 200 | [mg] |
| Limiting Pressure Velocity | 0.830 MPa-m/sec | 23700 psi-ft/min |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 62.0 µm/m-°C | 34.4 µin/in-°F | ASTM D696 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ASTM D696 |
| Melting Point | 300 °C | 572 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ISO 75-1/-2 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | 10°C/min; ISO 11357-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release Agent | |
| Applications | Automotive | |
| General Purpose | ||
| Chemical Resistance | Acid Resistance | |
| Alkali Resistance | ||
| Environmental Stress Crack Resistance | ||
| General Chemical Resistance | ||
| Grease Resistance | ||
| Hydrolytically Stable | ||
| Oil Resistance | ||
| Solvent Resistance | ||
| Delivery Form | Black | |
| Natural Color | ||
| Other Features | Barrier Properties | |
| Creep Resistance | ||
| High Crystalinity | ||
| Thermal Stability | ||
| Weldable | ||
| Processing | Injection Molding | |
| Regional Availability | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Special Characteristics | Heat Stabilized or Stable to Heat |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML6411 PC Copolymer
- Jackon JACKOCELL® R411 Expanded Polystyrene Packaging and Shape Molding
- LATI Latamid 66 H2 K/30 PA 66, 30% Carbon Fiber Reinforced, Heat Stabilized
- Shin-Etsu Silicones KF-9014 Fluid
- A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy
- ExxonMobil Exceed™ 1518HA Metallocene Polyethylene Resin
- Diamond Polymers NPP25-0616 Black Impact Modified Polypropylene
- BASF Procom® GC30S 401 Polypropylene
- Oceanchem Group n-Propyl Bromide (NPB)
- Hexcel® HexPly® M56 180°C (350°F) Out-of-Autoclave Curing Matrix, M56/37%/7581
Copyright © lookpolymers.com All Rights Reserved