- DSM EcoPaXX® Q-HGM24 PA410-(GF+MD)30
DSM EcoPaXX® Q-HGM24 PA410-(GF+MD)30
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | EcoPaXX® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM EcoPaXX® Q-HGM24 PA410-(GF+MD)30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass Reinforced, 20% Mineral Reinforced, Heat Stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.50 % | 1.50 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm | 0.0065 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 65.0 MPa | 9430 psi | cond; ISO 527-1/-2 |
| 95.0 MPa | 13800 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 2.5 % | 2.5 % | dry; ISO 527-1/-2 |
| 3.6 % | 3.6 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | cond; ISO 527-1/-2 |
| 8.00 GPa | 1160 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 115 MPa | 16700 psi | cond; ISO 178 |
| 175 MPa | 25400 psi | dry; ISO 178 | |
| Flexural Modulus | 4.40 GPa | 638 ksi | cond; ISO 178 |
| 6.65 GPa | 965 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 0.530 J/cm² @Temperature 23.0 °C |
2.52 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 48.0 µm/m-°C | 26.7 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
dry; IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Calculated Bio Based Carbon Content (%) | 70 | ASTM 6866 |
Users viewing this material also viewed the following:
- RheTech Products G10P100-01UV 10% Glass Fiber Reinforced Polypropylene, UV Stabilized, Black
- Pacific Sintered Materials SS-316-RH 316L Stainless Steel Powdered Metal
- LG Chemical LUCEL CF-620 Electrically Conductive POM, 20% Carbon Fiber Filled, High Strength, Wear Resistant
- Solvay Specialty Polymers Halar® 6014 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Solvay Technyl® A 205F Nylon 66, EH0
- Hexcel® HexWeb® CR-PAA™ 3/16-5056-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb
- Chevron Phillips K-Resin® DK11 Styrene-Butadiene Copolymer, Film Grade
- Chang Chun Plastic Longlite PM T310 Impact Phenolic Molding Compound
- PTS POM-270 Acetal Copolymer
Copyright © lookpolymers.com All Rights Reserved