- Solvay Technyl® C206F Unfilled, Fast Cycle Nylon 6
Solvay Technyl® C206F Unfilled, Fast Cycle Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® C206F Unfilled, Fast Cycle Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183-A |
| Water Absorption | 1.3 % | 1.3 % | 24 Hr.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 85.01 MPa | 12330 psi | ISO 527 |
| Elongation at Break | 120 % | 120 % | ISO 527 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.25 kJ/m² | 2.50 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 3146-C |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-2 |
| Flammability, UL94 | V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 220 - 230 °C | 428 - 446 °F | |
| Middle Barrel Temperature | 225 - 235 °C | 437 - 455 °F | Compression Zone |
| Front Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Nozzle Temperature | 229 - 249 °C | 445 - 480 °F | |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Fill Speed | 300 - 600 mm/sec | 11.8 - 23.6 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 50 - 150 cm3/sec |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP CGI11XP PS (Europe-Africa-Middle East)
- IBC Advanced Alloys FA230 Beryllium Nickel Casting Alloy
- LTL Color Compounds ColorFast® PAHF Polycarbonate-ABS Alloy
- IRPC Polimaxx Polene PE100N Polypropylene Wax
- H.C. Starck High Vacuum 250 Titanium Carbide, TiC
- Teknor Apex Monprene® MP-2830C CLR Thermoplastic Elastomer
- Teknor Apex Telcar® OBC 4975F Thermoplastic Elastomer
- A. Schulman POLYFORT™ PP 2268UX Heat Resistant Polypropylene
- Clariant Renol 6602-L Nylon 66, Internally Lubricated
- SABIC Innovative Plastics Lexan® HF1110 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved