A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer A. Schulman, Inc.
Trade Name SCHULAMID®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman SCHULAMID® 66 MV3FR Flame Retardant Nylon 6/6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D792
Linear Mold Shrinkage 0.011 cm/cm

@Thickness 3.175 mm
 0.011 in/in

@Thickness 0.1250 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.2 MPa
10900 psi
ASTM D638
Elongation at Break 5.5 %
5.5 %
ASTM D638
Flexural Strength 115 MPa
16700 psi
ASTM D790
Izod Impact, Unnotched 6.62 J/cm
12.4 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 230 °C
446 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.2 °C
189 °F
ASTM D648
Flammability, UL94 V-0
V-0
Processing Properties Metric English Comments
Melt Temperature 280 - 305 °C
536 - 581 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 2 - 4 hour
2 - 4 hour
Predrying