- Teijin Multilon DN-1520B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
Teijin Multilon DN-1520B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Teijin |
| Trade Name | Multilon |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Multilon DN-1520B Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 20 % filler. Improved stiffness and high fluidity realizes a thin wall of OA machines etc.Applications:Thin wall components of mechanical, electric and electronic equipment that need least warpage and dimensional accuracy etc.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 4.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 50mm/min; ISO 527 |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | 50mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 50mm/min; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 6.50 GPa | 943 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 115 MPa | 16700 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 6.20 GPa | 899 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 38.0 µm/m-°C @Temperature 20.0 °C |
21.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 48.0 µm/m-°C @Temperature 20.0 °C |
26.7 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ISO 75 |
| Vicat Softening Point | 124 °C | 255 °F | 50°C/hr, 50N; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
|
| V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
||
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® AT-1002 HS Polyphthalamide (PPA) (Unverified Data**)
- Imerys Kingsley - Rogersâ„¢ Kaolin
- LG Chemical LUMAX HF-5008 High Flow PBT, Dimensional Stability
- Inno-Comp INNOPOL® CS 2-9000 Polypropylene Block-Copolymer
- Gromax BFG50-BN00N1 Nylon 6 60% Glass Filled (Conditioned)
- Heatbath/Park AL-2 High Speed Hardening Salt
- Flint Hills P5M6N-058A Polypropylene Random Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific)
- Shandong Rike Chemical RIKEâ„¢ RK-870 MBS Impact Modifier for PVC Transparent Product
- Universal Wire Works 82 (AMS 5836) Filler Metal
Copyright © lookpolymers.com All Rights Reserved