Nilit FRIANYL B63 FK 1010 Nylon 6 for injection molding, 10% glass fiber and 10% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 FK 1010 Nylon 6 for injection molding, 10% glass fiber and 10% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.4 % | 1.5 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0080 - 0.017 cm/cm | 0.0080 - 0.017 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 150 MPa | 21800 psi | ISO 2039-1 |
| Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527 |
| Elongation at Break | 4.8 % | 4.8 % | ISO 527 |
| Tensile Modulus | 5.30 GPa | 769 ksi | ISO 527 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 4.30 GPa | 624 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.80 J/cm² | 18.1 ft-lb/in² | ISO 179/1eU |
| 3.60 J/cm² @Temperature -30.0 °C |
17.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.480 J/cm² | 2.28 ft-lb/in² | ISO 179/1eA |
| 0.360 J/cm² @Temperature -30.0 °C |
1.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 575 V | 575 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- MV Labs PT750 Pt(NH3)2(NO2)2 trans-Diaminedinitroplatinum(II)
- NOVA Chemicals Sclair® 10A Octene VLDPE Film Resin (discontinued **)
- Kuraray Genestarâ„¢ GX1500A-M41 Nylon, 50% Glass Filled
- Sekisui PIOCELAN LSP-40EB Moldable Polymer Foam
- Solvay RHODAPHOSE® TETRABUTYLPHOSPHONIUM HYDROXIDE Phosphorus Derivative
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 40 PHR N550 (FEF) Filler
- EPICHEM Epilac R ABS 10% GF Acrylonitrile Butadiene Styrene, 10% Glass Fiber
- Bohler-Uddeholm POLMAX® 420 Modified - Stainless Mold Steel
- Aclo Accutech Polypropylene Copolymer CP0436T20L1 Talc Reinforced
- DuPont Performance Polymers Rynite® 935 NC010 PET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved