- Lehmann & Voss LUVOCOM® 80-7626 Polyacetal-copolymer, with carbon fiber
Lehmann & Voss LUVOCOM® 80-7626 Polyacetal-copolymer, with carbon fiber
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 80-7626 Polyacetal-copolymer, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Electrically conductive, suitable for continuous discharging of statically generated electricity.No change of electric potential at bearings in case of separation of charge caused by transport and guiding of paper and foil.Transporting equipment for electrically sensible goods.No mass temperature above 215°C! Ventilation of machinery is recommended.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0090 - 0.014 cm/cm | 0.0090 - 0.014 in/in | |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 190 °C |
19 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 85.0 MPa | 12300 psi | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| 4.3 % | 4.3 % | flexural | |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | |
| Flexural Strength | 115 MPa | 16700 psi | |
| Flexural Modulus | 6.00 GPa | 870 ksi | |
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | flatwise; ISO 179 1fU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | HOT-DISK || 60x60x3 mm |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| 120 °C | 248 °F | short term | |
| Flammability, UL94 | HB | HB | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |
| Insulation Resistance | <= 1.00e+7 ohm | <= 1.00e+7 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | mass temp |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | |
| Zone 1 | 175 - 190 °C | 347 - 374 °F | |
| Zone 2 | 185 - 205 °C | 365 - 401 °F | |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 7200 - 28800 sec |
167 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| 120 °C @Time 7200 - 14400 sec |
248 °F @Time 2.00 - 4.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Nye Lubricants 782D (NG) Synthetic Oil
- LG Chemical LUPOY GN1000FA PC, Halogen Free, Flame Retardant, Transparency
- Lehmann & Voss LUVOCOM® 1100-8134 Polyether sulfone, with carbon fiber
- Sharadaa Ceramics ZAP 007 Smart Cast Application
- Techmer ES Luriblend® PA6 ML2 Nylon 6
- Shandong Dongyue Polymer DF-11 PTFE Molding Powder (Micronized Particles)
- Cytec EN-7 (Conap) Casting, Potting, and Molding Compound
- Hippe PF CP 32 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod
- BASF Ultramid® 8232G HS FR 25% Glass Fiber Fire Retardant PA6 (Conditioned)
- Arlon R37622X008 0.008" (0.203 mm) Cured Silicone Rubber with Release PET Carrier
Copyright © lookpolymers.com All Rights Reserved