Zircar Zirconia ZYC Zirconia Cylinders Insulation

Category Ceramic , Machinable Ceramic , Oxide , Zirconium Oxide
Manufacturer Zircar Zirconia
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zircar Zirconia ZYC Zirconia Cylinders Insulation.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zircar Zirconia Cylinders Type ZYC are rigid, free standing refractory structures composed of yttria stabilized zirconia fibers that are bonded with silica. The material is evenly bonded, allowing intricate shapes to be machined with tight tolerances. Type ZYC Cylinders possess low thermal conductivity and good resistance to thermal shock and are ideally suited for thermal insulation and protection applications under conditions of ultra-high temperatures and severe environments. ZYC is dimensionally stable to 1650°C although it can be used at higher temperatures in areas where additional sintering can be tolerated or as back-up insulation. It has good hot strength up to 1400°C. ZYC is resistant to attack by most molten metals and has a high resistance to reaction with other oxide materials. ZYC Cylinders are phase stabilized with yttria and therefore do not undergo the usual phase transitions associated with zirconia. Electrical conductivity at elevated temperatures is also minimized with low density Zirconia fibers whereas dense Zirconia is an effective conductor at elevated temperatures. ZYC does not couple with radio frequency (RF) radiation used in induction heating, but does couple with microwave energy. ZYC has no organic binders and will produce no smoke or odor when heated.Features: Rigid and Machinable Silica Bond for Thermal Shock Resistance Our Most Economical ZrO2 Cylinder Fibers Stabilized with ~10 wt% yttriaLow Thermal Conductivity Can be Cemented with Zircar Cement Type ZR-CEM Can be Surface Hardened with Zirconia Rigidizer Type ZR-RIG Pre-fired and Organic FreeInformation provided by Zircar Zirconia.
Physical Properties Metric English Comments
Bulk Density 0.480 g/cc
0.0173 lb/in³
Porosity 91 %
91 %
Outgassing - Total Mass Loss 0.00 %
0.00 %
In vacuum
Mechanical Properties Metric English Comments
Flexural Strength 0.550 MPa
79.8 psi
Parallel to thickness
Compressive Yield Strength 0.210 MPa
30.5 psi
Parallel to thickness @ 10% compression
Thermal Properties Metric English Comments
CTE, linear 9.00 µm/m-°C

@Temperature 20.0 - 950 °C
5.00 µin/in-°F

@Temperature 68.0 - 1740 °F
Thermal Conductivity 0.0800 W/m-K

@Temperature 400 °C
0.555 BTU-in/hr-ft²-°F

@Temperature 752 °F
0.110 W/m-K

@Temperature 800 °C
0.763 BTU-in/hr-ft²-°F

@Temperature 1470 °F
0.140 W/m-K

@Temperature 1100 °C
0.972 BTU-in/hr-ft²-°F

@Temperature 2010 °F
0.190 W/m-K

@Temperature 1400 °C
1.32 BTU-in/hr-ft²-°F

@Temperature 2550 °F
0.230 W/m-K

@Temperature 1650 °C
1.60 BTU-in/hr-ft²-°F

@Temperature 3000 °F
Melting Point 2200 °C
3990 °F
Maximum Service Temperature, Air 1650 °C
3000 °F
Continuous
1700 °C
3090 °F
Intermittent
Softening Point 950 °C
1740 °F
Dilatometric @ 10psi
Shrinkage 2.50 %

@Temperature 1650 °C,
Time 3600 sec
2.50 %

@Temperature 3000 °F,
Time 1.00 hour
perpendicular to thickness
4.00 %

@Temperature 1650 °C,
Time 86400 sec
4.00 %

@Temperature 3000 °F,
Time 24.0 hour
perpendicular to thickness
Component Elements Properties Metric English Comments
HfO2 1.0 - 2.0 %
1.0 - 2.0 %
Y2O3 10 %
10 %
ZrO2 83 - 84 %
83 - 84 %