Tra-Con Tra-Bond FS469 Clear High Strength Epoxy
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Tra-Con, Inc. |
| Trade Name | Tra-Bond |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tra-Con Tra-Bond FS469 Clear High Strength Epoxy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRA-BOND FS469 is a clear low viscosity epoxy formulation designed for bonding and coating micro-electronics, laminations, optical components and laser assemblies. The low cure shrinkage (using a room temperature cure) makes TRA-BOND FS469 and excellent choice to utilize in critical optic applications where alignment accuracy is essential. This high strength system is used for laminating glass and rigid plastics or bonding metals and ceramics. TRA-BOND FS469 offers superior resistance to mechanical shock and temperature cycling. It can also be used in temperature cycling applications where minimal stress is required.Information provided by Tra-Con Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | Mixed |
| Volatile Organic Compounds (VOC) Content | 12.93 g/l | 12.93 g/l | |
| Water Absorption | 0.86 % | 0.86 % | After 24 hours |
| Viscosity | 300 cP @Temperature 25.0 °C |
300 cP @Temperature 77.0 °F |
Mixed (sp #4, 30 rpm) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | 24 hrs @ 25°C |
| 80 | 80 | 4 hrs @ 65°C | |
| Adhesive Bond Strength | 11.0 MPa | 1600 psi | Lap shear, alum to alum, 24 hrs @ 25°C |
| 18.6 MPa | 2700 psi | Lap shear, alum to alum, 4 hrs @ 65°C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Minimum Service Temperature, Air | -70.0 °C | -94.0 °F | |
| Glass Transition Temp, Tg | 40.0 °C | 104 °F | Ultimate Tg |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 240 min @Temperature 65.0 °C |
4.00 hour @Temperature 149 °F |
|
| 1440 min @Temperature 25.0 °C |
24.0 hour @Temperature 77.0 °F |
||
| Pot Life | 120 min | 120 min | 25 grams |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Clear | |
| Mix Ratio, parts by weight | 100/30 | Resin/Hardener |