Tra-Con Tra-Bond 216R01 Fire Retardant Epoxy

Category	Polymer , Adhesive , Thermoset , Epoxy
Manufacturer	Tra-Con, Inc.
Trade Name	Tra-Bond
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Tra-Con Tra-Bond 216R01 Fire Retardant Epoxy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TRA-BOND 216R01 is a fast curing material with a set time of 5 to 7 minutes. Samples tested were certified to the requirements of UL94 V-O, and is RoHS compliant. TRA-BOND 216R01 develops significant properties 1 hour after mixing. However, an extended cure of 4-6 hours at 25°C is required for fully matured bonds. Note: TRA-BOND 216R01 develops a high exotherm. Use immediately after mixing. The exothermic reaction begins within 2 minutes after initiating the mixing step, so have everything ready before removing the BIPAX clamp.Information provided by Tra-Con Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.20 g/cc	1.20 g/cc	Mixed
Viscosity	23000 cP	23000 cP	Hardener (cp #52, 10 rpm)
	45000 cP	45000 cP	Resin (cp #52, 10 rpm)

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	84	84	2 hrs @ 65°C
Adhesive Bond Strength	24.8 MPa	3600 psi	Lap shear, alum to alum, 24 hrs @ 25°C
	31.0 MPa	4500 psi	Lap shear, alum to alum, 2 hrs @ 65°C

Thermal Properties	Metric	English	Comments
Glass Transition Temp, Tg	38.0 °C	100 °F	Ultimate Tg; DSC
Flammability, UL94	V-0 @Thickness 6.35 mm	V-0 @Thickness 0.250 in

Processing Properties	Metric	English
Cure Time	60.0 min @Temperature 65.0 °C	1.00 hour @Temperature 149 °F
	240 - 360 min @Temperature 25.0 °C	4.00 - 6.00 hour @Temperature 77.0 °F
Pot Life	5.0 min	5.0 min

Descriptive Properties	Value	Comments
Color	Cream
Mix Ratio, parts by weight	100/93	Resin/Hardener