Physical Properties Metric English Comments
Viscosity 45000 cP

@Pressure 0.621 MPa
45000 cP

@Pressure 90.0 psi
Servers; ASTM D-1823
SABIC PVC 701E Emulsion Polyvinyl Chloride for Paste Preparation
Product Description: PVC 701E is a fine particle, medium-molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting high viscosi..
Viscosity 45000 cP

@Pressure 0.621 MPa
45000 cP

@Pressure 90.0 psi
Servers; ASTM D-1823
SABIC PVC 741E Emulsion Polyvinyl Chloride for Paste Preparation
Product Description: PVC 741E is a fine particle, high molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting low viscositie..
Viscosity 45000 - 65000 cP

@Temperature 40.0 °C
45000 - 65000 cP

@Temperature 104 °F
Taiwan PU Corporation PTMG CPU-42L Polyurethane Casting Elastomer
A urethane elastomer that can be cured by reacting with a polyamine or a polyolhardener. The molding process is composed of pre-heating, degassing, maxing with a hardener, pouring into the mold, cu..
Viscosity 45000 cP
45000 cP
Before Curing
Silikony Polskie Gumosil M Silicone Rubber
Flexible with good tearing resistance
Viscosity 45000 cP
45000 cP
Master Bond Mastersil 800 One Component, Room Temperature Curing Silicone
MasterSil 800 is an easy to use, one component, high performance silicone elastomer compound for bonding, sealing, coating and formed-in-place gaskets. This specialty system features ultra high temp..
Viscosity 45000 cP
45000 cP
Haake cone and plate rheometer @ 5/sec (35mm/2° cone)
Loctite® 3565 High performance epoxy, high Tg and low CTE High Tg Underfill
COB/DCA Encapsulants are essential to the reliability of flip chip assemblies because they minimize the thermal mismatch between the flip chip and substrate.Loctite® Underfills and Encapsulants imp..
Viscosity 45000 - 75000 cP
45000 - 75000 cP
Part A
Master Bond EP30LTE-LO Dimensionally Stable Low Outgassing Two Part Epoxy
Master Bond Polymer System EP30LTE-LO is a thermal shock resistant epoxy resin system with low thermal expansion properties and dimensional stability for high performance bonding, sealing and castin..
Viscosity 45000 cP
45000 cP
Resin (cp #52, 10 rpm)
Tra-Con Tra-Bond 216R01 Fire Retardant Epoxy
TRA-BOND 216R01 is a fast curing material with a set time of 5 to 7 minutes. Samples tested were certified to the requirements of UL94 V-O, and is RoHS compliant. TRA-BOND 216R01 develops significa..
Viscosity 45000 cP
45000 cP
dynamic
Dow Corning 736 HEAT RESISTANT/SEALANT
Red RTV adhesive/sealant for temperatures up to 600F/315CInformation provided by Dow Corning
Viscosity 45000 cP

@Temperature -30.0 °C
45000 cP

@Temperature -22.0 °F
ConocoPhillips Syncon® 50 Synthetic Transmission Oil, ISO Grade
Description: Conoco Syncon HP Synthetic Transmission Oil is a synthetic lubricant for heavy-duty manual transmissions, with or without synchronizers. It is approved by Eaton Corp. as an alternative ..
Viscosity 45000 - 55000 cP
45000 - 55000 cP
dynamic
Dow Corning Q3-3559 SEMIFLOWABLE TEXTILE ELASTOMER
A semi-flowable 1 part solventless silicone elastomer.Information provided by Dow Corning
Viscosity 45000 cP

@Temperature 25.0 °C
45000 cP

@Temperature 77.0 °F
Cytec (Conap) RN-1210 / EA-87 Conapoxy® Resin / Conacure® Hardener
Epoxy Potting and Encapsulating Systems for Electronic ApplicationsHigh technology epoxy resin systems for potting and encapsulation, for the defense, aerospace, electronics, computer, automotive an..
Viscosity 45000 - 70000 cP

@Temperature 23.0 °C
45000 - 70000 cP

@Temperature 73.4 °F
50 rpm
Epoxy Technology EPO-TEK® OE100-T High Temperature Epoxy
Material Description: A two component, high Tg, high temperature grade epoxy designed for semiconductor, underfill, hard-disk drive and hybrid micro-electronics packaging applications. The epoxy ca..
Viscosity 45000 cP
45000 cP
Epoxyset Epoxibond EB-347 Low Expansion Epoxy Adhesive
EB-347 is a highly filled, low coefficient expansion, epoxy adhesive. This low out-gassing adhesive exhibits excellent wettability without preheating metal bonding surfaces and has a good dimensiona..
Viscosity 45000 cP
45000 cP
dynamic
Dow Corning 3-3442 FLOWABLE TEXTILE SEALANT
A flowable one part acid curing rtv silicone for elastomeric coatings.Information provided by Dow Corning
Viscosity 45000 cP
45000 cP
Dymax 9003v3.0 Flexible Clear Microencapsulant
High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9003v3.0 Flexible Clear MicroencapsulantGlob top for photosensing devices Cure Type: UV/Visible Typical Use: Optic..
Viscosity 45000 cP
45000 cP
ACC MM850 Low Tear Condensation Cure 2-Part Molding Rubber
Part of the Amber Chemical Group. Data provided by manufacturer.Characteristics: low viscosity, good resistance to styrene attack, easy degassing, low shrinkage, range of catalysts. Applications: sh..
Viscosity 45000 cP
45000 cP
Base
ACC QM 135 QSI Quantum Silicones 35 Durometer Condensation Cured Moldmaking Material
QM 135 is a two-component, room temperature condensation cure silicone material. The cured rubber has excellent mechanical properties and good shelf-life stability. This material is an excellent cho..
Viscosity 45000 cP
45000 cP
B Component; ASTM D1824
Aptek 2201-A/B Fast set urethane adhesive
APTEK 2201-A/B is a two component, dark gray, urethane adhesive system displaying excellent adhesion to various plastic, wood, ceramic, and metal substrates. APTEK 2201-A/B is capable of achieving f..
Viscosity 45000 - 85000 cP
45000 - 85000 cP
3M Scotch-Weld™ CA50 Gel Instant Adhesive
3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. High-viscosity, non-sag gel and less sensitive to acidic surfaces.Information provided by 3M
Viscosity 45000 cP
45000 cP
Mixed Viscosity
Aremco Aremco-Bond™ 2310 High Performance Epoxide
Ceramic-Filled, 1:1, High Lap Shear and Peel Strength, Autoclavable.
Viscosity 45000 - 85000 cP
45000 - 85000 cP
3M Pronto™ CA-50 Gel Instant Adhesive
One-part, room-temperature curing adhesive that is ready-to-use without metering or mixing. Bonded parts reach handling strength in 5-10 seconds on many applications.A high-viscosity gel consistenc..
Viscosity 45000 cP
45000 cP
Base
ACC QM 262 QSI Quantum Silicones 60 Durometer Addition Cure Moldmaking Material
QM262 is a two component, room temperature, addition cure silicone material. The cured rubber has excellent mechanical properties, good shelf-life stability, excellent physical properties and resin ..
Viscosity 45000 cP

@Temperature 25.0 °C
45000 cP

@Temperature 77.0 °F
Mixed
Trelleborg Emerson & Cuming Stycast® 4640-25 Two-Component Silicone Flexible Encapsulant
Emerson & Cuming 4640-25 Stycast® Two-Component Silicone Flexible EncapsulantDescriptionAn RTV condensation cure. Pourable and room temperature curable.FeaturesHigh TemperaturePoor Chemical Resista..
Viscosity 45000 cP
45000 cP
Part A, RVT, #7, 20 rpm; TM R050-12
Resinlab® EP1305LV Clear Epoxy Casting Resin
Resinlab™ EP1305LV Clear is a black two-part epoxy casting resin designed to give good adhesion to metals and especially PVC. It has good wetting to most surfaces and is free flowing to penetrate c..