Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir R 321P Polystyrene Medium impact polystyrene combining easy flow and high stiffness. For injection moulding of parts with low thickness and high rigidity. Designation: Thermoplastics ISO 2897-PS-I,M,083-12-04-30Applic.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir R 540E Polystyrene HIPS with high stiffness, matt surface finish and good heat resistance. Suitable for general extrusion of thick sheets and profiles. Also used for injection
moldings. Designation: Thermoplastics IS.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50mm/min; ASTM D638 |
Reliance Industries Repol B550MN Polypropylene REPOL Polypropylene B550MN is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50mm/min; ASTM D638 |
Reliance Industries Repol B120MA Polypropylene REPOL Polypropylene B120MA is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
Braskem BT 003 HDPE Blow Molding Polyethylene
(discontinued **) Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
LyondellBasell Astryn BC78A Polypropylene Copolymer, 23% Talc Key Features: high melt flow, high modulus, mineral-filled polypropylene copolymer, high rigidity, good colorability, good processabilityApplications: automotive interior trim components, pillar mol.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO-DIS 527 |
Schwartz Technical Plastics LAMIGAMID® 710 High Density Polyethylene Application: chain-guides, cutting plates, linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MB006S PP LNP THERMOCOMP* MB006S is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50mm/min; ISO 527-2 |
Borealis BC612WG Polypropylene Copolymer BC612WG is a polypropylene copolymer intended for injection molding. The product is available in natural but other colors can be provided on request. This material has excellent balanced mechanical.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50mm/min; ISO 527-2 |
Borealis MG7547S Polyethylene MG7547S is a high-density polyethylene produced by a low pressure process. This grade has an excellent impact strength and low distortion even at low temperatures. It also contains UV stabilizer, wh.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU Toyota is a high flow copolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | at 50 mm/min; ASTM D638 |
A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
Tipco Tipcolene® DR 8201 - 20% Talc/Mineral Reinforced, Impact Modified, Polypropylene Copolymer 20% Mineral Reinforced, Impact Modified PP Copolymer BlendApplications: Automotive DashboardsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
Tipco Tipcolene® FPT 30 BK CP - 30% Talc Polypropylene Homopolymer, Special Heat Stability 30% Talc Reinforced PP Homopolymer with Special AdditivesApplications: AutomotivesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 |
Tisan TISOPLEN® 10% Calcite Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1245U CaCO3 Filled UV Stable Copolymer Polypropylene DescriptionPolyfort® FPP 1245U is a 20% CAC03 filled UV stable copolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 - 27.0 MPa | 3480 - 3920 psi | ASTM D638 |
A. Schulman POLYFLAM™ CFP 4623 20% Calcium Filled Polypropylene DescriptionPolyfort® 4623 is a 20% calcium filled polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 |
Total PPC 11812 S01 Polypropylene, Heterophasic Copolymer, Injection Molding Polypropylene PPC 11812 S01 has been developed for high speed injection molding of thin walled packaging containers requiring top level impact resistance at cold temperature (-20°C). It is charact.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
Entec Hypro™ PP-CP20/10 Impact Copolymer, 20 Melt Flow This product is intended for general purpose injection molding applications including flooring, automotive, appliance, lawn and garden and industrial application.Information provided by Entec |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO R 527 |
Addiplast Addilene J 520 M40 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50 mm/min; ASTM D638 |
Carmel Olefins CAPILENE® SE 50 E Polypropylene Impact Copolymer Description: CAPILENE® SE 50 E is a low melt flow rate impact copolymer intended for sheet extrusion. It exhibits excellent impact strength even at low temperatures, combined with good processabi.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50 mm/min; ASTM D638 |
Carmel Olefins CAPILENE® SW 75 AV Polypropylene Impact Copolymer Description: CAPILENE® SW 75 AV is a high melt flow rate, controlled rheology impact copolymer for injection molding. CAPILENE® SW 75 AV is nucleated with antistatic additivation. It is characte.. |
|||
Tensile Strength, Yield | 24.0 - 34.0 MPa | 3480 - 4930 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 3120-15 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible, flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO R 527-2 |
Arkema Group OREVAC® 18760 Grafted Maleic Anhydride Polypropylene OREVAC 18760 is a maleic anhydride grafted polypropylene used in the manufacturing of three layer PP coating for steel pipeline. OREVAC 18760 is also used in multilayer EVOH – PP structures. OREVAC.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
Aclo Accuguard Polypropylene HPN469V2CSL Homopolymer Non-Halogenated Copper Stabilized |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM-D638 |
Braskem IG58 HDPE Injection Molding Polyethylene Copolymer IG58 is a high-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high stiffness, impact strength and out.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO R 527 |
Addiplast Addilene J 220 M40 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | |
BASF Procom® T20C 557 Polypropylene Car interior trim panels.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 |
Total Lacqtene® 2001 TN 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TN 46 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2001 TN 46 is used for sewage pipe, smooth protective condu.. |
|||
Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
LyondellBasell Pro-fax SV152 Polypropylene Impact Copolymer Key Features: fast crystallization shortens cycle times, excellent cold impact resistance, good stiffness and impact balance, FDA acceptableApplications: automotive blow molded partsMeets FDA requir.. |