Polymer Property : Tensile Strength, Yield = 24.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	24.0 MPa	3480 psi	50 mm/min; ISO 527
Polimeri Europa Edistir R 540E Polystyrene HIPS with high stiffness, matt surface finish and good heat resistance. Suitable for general extrusion of thick sheets and profiles. Also used for injection moldings. Designation: Thermoplastics IS..
Tensile Strength, Yield	24.0 MPa	3480 psi	50mm/min; ASTM D638
Reliance Industries Repol B550MN Polypropylene REPOL Polypropylene B550MN is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly..
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
SABIC M40060 Series High Density Polyethylene for Injection Molding Product Description: M40060 is a high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to provide good rigid..
Tensile Strength, Yield	24.0 MPa	3480 psi	2.0 in/min; ASTM D638
Ineos Nova 850 High Performance Styrenic Enhanced Polystyrene (discontinued **) Extremely high impact strength with good flexural stiffness, Custom colorsApplications: Injection molding or extrusion, Suitable replacement for some engineering resins, Toys, Packaging, Business eq..
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
Flint Hills P9M6K-041A Specialty Impact Copolymer Polypropylene Features: Good clarity and impact resistance. Product does not contain animal derived components.Applications: Injection molding - durable goodsInformation provided by Flint Hills Resources.
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
LyondellBasell Astryn BC78A Polypropylene Copolymer, 23% Talc Key Features: high melt flow, high modulus, mineral-filled polypropylene copolymer, high rigidity, good colorability, good processabilityApplications: automotive interior trim components, pillar mol..
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU Toyota is a high flow copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	24.0 MPa	3480 psi	50mm/min; ISO 527-2
Borealis BB125MO Polypropylene Copolymer BB125MO is a heterophasic copolymer. This grade is a low melt flow rate grade intended for blow molding and sheet extrusion, and features extremely good process ability with improved melt strength a..
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1245 is a 20% CAC03 filled copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	24.0 MPa	3480 psi	at 50 mm/min; ASTM D638
A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman.
Tensile Strength, Yield	24.0 MPa	3480 psi	2 in/min; ASTM D638
A. Schulman PP 3457-01 Copolymer Polypropylene DescriptionPolypropylene PP 3457-01 is a copolymer polypropylene combining high impact at cold temperatures while maintaining stiffness. Ideal for durables in such applications for the furniture, a..
Tensile Strength, Yield	24.0 MPa	3480 psi	at 50 mm/min; ASTM D638
A. Schulman POLYFORT™ PP 3726 Information provided by A. Schulman.
Tensile Strength, Yield	24.0 MPa	3480 psi	2 in/min; ASTM D638
A. Schulman PP 3457-01 Copolymer Polypropylene DescriptionPolypropylene PP 3457-01 is a copolymer polypropylene combining high impact at cold temperatures while maintaining stiffness. Ideal for durables in such applications for the furniture, a..
Tensile Strength, Yield	24.0 MPa	3480 psi	ISO 527
Total 49080 UV HDPE blow molding FINATHENE® 49080 UV is produced by the slurry loop low pressure polymerization process. FINATHENE® 49080 UV is a U.V.-stabilized, high molecular weight pelletized resin, intended for the productio..
Tensile Strength, Yield	24.0 MPa	3480 psi	ISO 527-2
Total PPC 3666 Polypropylene, Heterophasic Copolymer, Extrusion Polypropylene PPC 3666 is a heterophasic copolymer with a Melt Flow index of 1.5 g/10 min. This resin offers an outstanding processability in combination with good melt strength and excellent mecha..
Tensile Strength, Yield	24.0 MPa	3480 psi	ISO 527-2
Total PPC 7760 Polypropylene, Heterophasic Copolymer ATOFINA Propylene 7760 is a heterophasic copolymer. PPC 7760 is characterized by medium fluidity offering a combination of ease of processing and excellent impact properties in applications ranging..
Tensile Strength, Yield	24.0 MPa	3480 psi	ISO 527-2
Total PPC 9612 Polypropylene, Heterophasic Copolymer, Injection Molding This product is a Total Ecosolutions grade.Polypropylene PPC 9612 has been developed specifically for the injection molding of crates and is characterized by a high Melt Flow index of 20 g/10 min. ..
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1245 is a 20% CAC03 filled copolymer polypropylene product. Information provided by A. Schulman.
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
A. Schulman POLYFORT™ FPP 2496 Injection Molding Grade, Mineral Fortified Polypropylene DescriptionPolyfort® FPP 2496 is an injection molding grade mineral fortified and impact enhanced polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	24.0 - 27.0 MPa	3480 - 3920 psi	ASTM D638
A. Schulman POLYFLAM™ CFP 4623 20% Calcium Filled Polypropylene DescriptionPolyfort® 4623 is a 20% calcium filled polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene DescriptionPolyfort® PP 2175HU-31 is a high flow copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	24.0 MPa	3480 psi	2 in/min; LAB032
ExxonMobil Mytex™ AS65KW-1ATM Talc filled compounded polypropylene produced for automotive interior applicationsInformation provided by ExxonMobil Chemical
Tensile Strength, Yield	24.0 MPa	3480 psi	ISO R 527
Arkema Group OREVAC® 18751 Maleic Anhydride Modified Polypropylene DescriptionOREVAC 18751 is a coextrusion coating adhesive based on a maleic anhydride modified polypropylene resin. It combines the processability of an extrusion coating resin with the thermal resi..
Tensile Strength, Yield	>= 24.0 MPa	>= 3480 psi	ASTM D638
Buckeye Polymers BP RPP 4012 T BLK Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and ..
Tensile Strength, Yield	24.0 MPa	3480 psi	50 mm/min; ASTM D638
Carmel Olefins CAPILENE® SU 75 AV Polypropylene Impact Copolymer Description: CAPILENE® SU 75 AV is a high melt flow rate, controlled rheology impact copolymer for injection molding. CAPILENE® SU 75 AV is nucleated with antistatic additive. It offers outstand..
Tensile Strength, Yield	24.0 MPa @Temperature 120 °C	3480 psi @Temperature 248 °F	ASTM Test
BASF Ultramid® 8270 HS PA6 (Dry) Ultramid 8270 HS is a thermally modified PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requi..
Tensile Strength, Yield	24.0 MPa	3480 psi	50 mm/min
Arkema Group Rilsan® AESN P40 TL Nylon 12, Flexible Tubing Grade (Conditioned) Designation ISO 1874-PA12-P,EHL,22-004Flexible grade for tubes extrusion. Available colors: black and natural. Light and heat stabilized.High impact strength. High burst pressure. Very good chemical..
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM-D638
Braskem IG58 HDPE Injection Molding Polyethylene Copolymer IG58 is a high-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high stiffness, impact strength and out..
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
A. Schulman POLYFORT™ FPP 2496 Injection Molding Grade, Mineral Fortified Polypropylene DescriptionPolyfort® FPP 2496 is an injection molding grade mineral fortified and impact enhanced polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	24.0 MPa	3480 psi	ASTM D638
IRPC Polimaxx Polene 3375RM Polypropylene Random Copolymer CHARACTERISTICS: GOOD EXTRUDABILITY, GOOD ADHESIVE, HIGH SPEED APPLICATIONS: EXTRUSION COATING FOR COATED WOVEN BAGS AND TARPAULINS