Teknor Apex Chemlon® 104 Nylon 66, Impact Grade
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 104 Nylon 66, Impact Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: Medium-Impact; General Purpose; Impact modified to provide excellent toughness Processing Method: Injection Molding Forms: Pellets Automotive Specifications: Chrysler MS-DB41 CPN3992 Color: WL5Information Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.012 - 0.020 cm/cm | 0.012 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
| Flexural Modulus | 2.21 GPa | 320 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm @Temperature -40.0 °C |
2.60 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 2.40 J/cm @Temperature 22.8 °C |
4.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.2 µm/m-°C | 39.0 µin/in-°F | ASTM D696 |
| Melting Point | 257 °C | 495 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.810 mm |
149 °F @Thickness 0.0319 in |
UL 746 |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0590 in |
UL 746 | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.810 mm |
149 °F @Thickness 0.0319 in |
UL 746 |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0590 in |
UL 746 | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.810 mm |
149 °F @Thickness 0.0319 in |
UL 746 |
| 65.0 °C @Thickness 1.50 mm |
149 °F @Thickness 0.0590 in |
UL 746 | |
| 65.0 °C @Thickness 3.00 mm |
149 °F @Thickness 0.118 in |
UL 746 | |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
|
| Oxygen Index | 22 % | 22 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.9 kV/mm @Thickness 3.00 mm |
430 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 - 254 °C | 465 - 490 °F | |
| Middle Barrel Temperature | 257 - 274 °C | 495 - 525 °F | |
| Front Barrel Temperature | 263 - 282 °C | 505 - 540 °F | |
| Nozzle Temperature | 263 - 279 °C | 505 - 535 °F | |
| Melt Temperature | 263 - 279 °C | 505 - 535 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |