Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 72.4 MPa | 10500 psi | Stress at 5% Strain, Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
Network Polymers PC-1004 Description: Natural PolycarbonateInformation provided by Network Polymers Inc. |
|||
Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
Polymer Resources PPX-GP3-IM Modified-PPO, Impact Modified Modified-Polyphenylene Oxide, Impact Modified, 235F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
Polymer Resources PC/ABS-GP1-[color]-3 PC Blend, General Purpose, UV-stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
Fiberfil® J-60/10/E Polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
Flexural Strength | 72.4 MPa @Temperature 149 °C |
10500 psi @Temperature 300 °F |
|
Greene Tweed Arlon® 1000 Polyketone Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie.. |
|||
Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
Techmer ES HiFill® POM CO 0374 S Acetal Availability: North AmericaForms: PelletsFiller/Reinforcement: MetalFeatures: CopolymerInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
Techmer ES Plaslube® PC-50/TF/13/SI/2 NAT Polycarbonate |
|||
Flexural Strength | 72.6 MPa | 10500 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® TF-0956 HI-PMMA Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 72.6 MPa | 10500 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® TF-0956 HI-PMMA Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
Techmer ES Plaslube® PC-50/TF/13/SI/2 WT8966 Polycarbonate |
|||
Flexural Strength | 72.4 MPa | 10500 psi | ASTM D638 |
Plastics Group Polifil® GFPP-30 30% Glass-Reinforced Polypropylene Polifil® GFPP series compounds are homopolymer polypropylene resins reinforced with glass fibers. They provide high impact with increased strength, stiffness, surface hardness, and higher continuou.. |
|||
Flexural Strength | 72.4 MPa | 10500 psi | Compared to 500 for concrete |
Abatron AboCrete Cement/Grout Resurfacing and Patching Epoxy Cement/grout resurfacing and patching epoxy for industrial, marine, institutional, and residential uses. The ultimate restoration and resurfacing material structurally and chemically superior to co.. |
|||
Flexural Strength | 72.4 MPa @Thickness 3.17 mm |
10500 psi @Thickness 0.125 in |
ASTM D790 |
Calsak CS-72L General Purpose ABS Resin Product Characteristics:High Impact, High GlossInjection molding grade |
|||
Flexural Strength | 72.4 MPa | 10500 psi | ASTM D-790 |
Axiall 7768 Rigid PVC, Extrusion Georgia Gulf 7768 is a general purpose rigid PVC profile extrusion compound designed for applications requiring the following properties: Impact Strength & ToughnessFlame RetardantColorabilityDimen.. |
|||
Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
Chase Plastics CP Pryme® PCA100 Polycarbonate/ABS Alloy Information provided by Chase Plastics. |