Sumitomo Bakelite North America 73-70-70 C-P /73-70-70 VO-P Short-Glass Reinforced Diallyl Phthalate

Category	Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset
Manufacturer	Sumitomo Bakelite North America
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sumitomo Bakelite North America 73-70-70 C-P /73-70-70 VO-P Short-Glass Reinforced Diallyl Phthalate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SDG-F.Information provided by Sumitomo Bak North America, Inc.

Physical Properties	Metric	English	Comments
Density	1.91 g/cc	0.0690 lb/inÂ³	ASTM D792
Apparent Bulk Density	0.800 g/cc	0.0289 lb/inÂ³
Water Absorption	0.25 %	0.25 %	48 hours, 50Â°C. ASTM D570
Linear Mold Shrinkage	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	Compression Molding. ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	76.0 MPa	11000 psi	ASTM D638
Flexural Yield Strength	124 MPa	18000 psi	ASTM D790
Flexural Modulus	11.7 GPa	1700 ksi	ASTM D790
Compressive Yield Strength	150 MPa	21800 psi	ASTM D695
Izod Impact, Notched	0.320 J/cm	0.599 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	21.0 Âµm/m-Â°C @Temperature 20.0 Â°C	11.7 Âµin/in-Â°F @Temperature 68.0 Â°F	ASTM D696
Thermal Conductivity	0.293 W/m-K	2.03 BTU-in/hr-ftÂ²-Â°F	ASTM F433
Maximum Service Temperature, Air	130 Â°C	266 Â°F	UL temperature Index, UL 746B
Deflection Temperature at 1.8 MPa (264 psi)	>= 260 Â°C	>= 500 Â°F	ASTM D648A
UL RTI, Electrical	130 Â°C	266 Â°F	UL temperature Index, UL 746B
UL RTI, Mechanical with Impact	130 Â°C	266 Â°F	UL temperature Index, UL 746B
UL RTI, Mechanical without Impact	130 Â°C	266 Â°F	UL temperature Index, UL 746B
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Oxygen Index	45 %	45 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.5 @Frequency 1e+6 Hz	3.5 @Frequency 1e+6 Hz	Wet
	4.2 @Frequency 1000 Hz	4.2 @Frequency 1000 Hz	Wet
Dielectric Strength	13.8 kV/mm @Frequency 60.0 Hz	351 kV/in @Frequency 60.0 Hz	Wet, step by step; ASTM D149
Dissipation Factor	0.010 @Frequency 1000 Hz	0.010 @Frequency 1000 Hz	Wet; ASTM D150
	0.014 @Frequency 1e+6 Hz	0.014 @Frequency 1e+6 Hz	Wet; ASTM D150
Arc Resistance	130 sec	130 sec	ASTM D495
Comparative Tracking Index	>= 600 V	>= 600 V	UL746A, ASTM D3638
Hot Wire Ignition, HWI	60 - 119 sec @Thickness 1.60 mm	60 - 119 sec @Thickness 0.0630 in	UL PLC 1 (60-119 sec)
High Amp Arc Ignition, HAI	<= 14 arcs @Thickness 1.60 mm	<= 14 arcs @Thickness 0.0630 in	UL PLC 4 (0-14 arcs)
High Voltage Arc-Tracking Rate, HVTR	0.000 - 10.0 mm/min @Thickness 1.60 mm	0.000 - 0.394 in/min @Thickness 0.0630 in	UL PLC 0 (0-10 mm/min)

Processing Properties	Metric	English	Comments
Processing Temperature	160 - 180 Â°C	320 - 356 Â°F	Mold temperature

Descriptive Properties	Value	Comments
Flammability, Burning, sec	15	ASTM D229
Flammability, Ignition, sec	115	ASTM D229