Styrolution Terblend® N NM-12 ABS/PA6 (Dry)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Styrolution |
| Trade Name | Terblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terblend® N NM-12 ABS/PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terblend N NM-12 is an ABS/PA6 blend combining high impact strength and rigidity with an excellent processability and surface appearance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 23°C/50% R.H.; ISO 62 |
| Melt Flow | 23 g/10 min @Load 10.0 kg, Temperature 240 °C |
23 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.0 MPa | 5660 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50mm/min; ISO 527 |
| 50.0 MPa | 7250 psi | 2 in/min; ASTM Test | |
| Elongation at Break | >= 30 % | >= 30 % | 0.2 in/min; ASTM Test |
| 40 % | 40 % | 50mm/min, Nominal strain; ISO 527 | |
| Elongation at Yield | 3.2 % | 3.2 % | 50mm/min; ISO 527 |
| Tensile Modulus | 2.28 GPa | 331 ksi | ASTM Test |
| 2.30 GPa | 334 ksi | 1mm/min; ISO 527 | |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO Data |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 |
| 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ISO 75 |
| Vicat Softening Point | 112 °C | 234 °F | (50 °C/h / 50N) - B/50; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 100 Hz |
3.3 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 41.0 kV/mm | 1040 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 265 °C | 509 °F | Injection molding |
| Injection Velocity | 65.0 mm/sec | 2.56 in/sec | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Active America | |
| Primary Processing Technique | Injection Molding | |
| UL.UL-C | Yes |