Solvay Specialty Polymers Ixef® 1622 Polyarylamide (PARA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 1622 Polyarylamide (PARA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef 1622 is an impact modified, 50% glass-fiber reinforced polyarylamide. which exhibits very high strength and rigidity, outstanding surface gloss, and excellent impact resistance. - Natural: Ixef 1622/0003 - Black: Ixef 1622/9003 - Custom ColorableAdditional Information: Unless otherwise specified, Typical Values are obtained from Dry (also called DAM, Dry as Molded) samples. For Conditioned data, samples are tested at 50% Relative Humidity.Injection Notes: Hot Runners: 250°C to 260°C (482°F to 500°F) Injection Pressure: rapid Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding IXEF 1622 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 270°C (518°F), and the barrel temperatures should be around 250°C to 260°C (482°F to 500°F) in the rear zone, gradually increasing to 260°C to 280°C (500°F to 536°F) in the front zone. If hot runners are used, they should be set to 250°C to 260°C (482°F to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120°C and 140°C (248°F and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95%-99%).Data is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber Reinforcement
Water Absorption 0.19 %

@Temperature 23.0 °C,
Time 86400 sec
0.19 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
65% RH; Internal Method
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Internal Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 235 MPa
34100 psi
ISO 527-2
Tensile Strength, Yield 200 MPa
29000 psi
Conditioned; ISO 527-2
Elongation at Break 2.6 %
2.6 %
ISO 527-2
2.7 %
2.7 %
Conditioned; ISO 527-2
Tensile Modulus 16.0 GPa
2320 ksi
Conditioned; ISO 527-2
17.0 GPa
2470 ksi
ISO 527-2
Flexural Strength 360 MPa
52200 psi
ISO 178
Flexural Modulus 17.0 GPa
2470 ksi
ISO 178
Izod Impact, Notched 1.20 J/cm
2.25 ft-lb/in
ASTM D256
11.0 J/cm
20.6 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 220 °C
428 °F
Annealed; ISO 75-2/A
Flammability, UL94 V-0
V-0
UL 94
Oxygen Index 25 %
25 %
ISO 4589-2
Electrical Properties Metric English Comments
Dielectric Constant 4.23

@Frequency 1.00e+9 Hz
4.23

@Frequency 1.00e+9 Hz
Method B; ASTM D2520
4.27

@Frequency 2.40e+9 Hz
4.27

@Frequency 2.40e+9 Hz
Method B; ASTM D2520
Dielectric Strength 25.0 kV/mm
635 kV/in
IEC 60243-1
Dissipation Factor 0.0095

@Frequency 1.00e+9 Hz
0.0095

@Frequency 1.00e+9 Hz
Method B; ASTM D2520
0.0095

@Frequency 2.00e+9 Hz
0.0095

@Frequency 2.00e+9 Hz
Method B; ASTM D2520
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 280 °C
500 - 536 °F
Melt Temperature 270 °C
518 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C
248 °F
Dry Time 0.500 - 1.50 hour
0.500 - 1.50 hour
Descriptive Properties Value Comments
Additive Impact Modifier
Appearance Black
Colors Available
Natural Color
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
High Flow
High Stiffness
High Strength
Impact Modified
Low Moisture Absorption
Outstanding Surface Finish
Forms Pellets
Generic PARA
Processing Method Injection Molding
RoHS Compliance RoHS Compliant
Uses Appliance Components
Appliances
Automotive Applications
Automotive Electronics
Business Equipment
Camera Applications
Electrical Housing
Electrical/Electronic Applications
Furniture
Gears
Housings
Industrial Applications
Lawn and Garden Equipment
Machine/Mechanical Parts
Metal Replacement
Power/Other Tools
Copyright © lookpolymers.com All Rights Reserved