Material Notes:
Seals Eastern's formulated Viton® elastomers can be utilized in seals, o-rings, gaskets, packings and other applications where thermal stability and chemical resistance are required.Features:Type 3 (Viton GFLT)Low temperature serviceFuel and chemical resistanceViton® is a registered trademark of DuPont. Information provided by Seals Eastern.
Physical Properties Metric English Comments
Specific Gravity 1.89 g/cc
1.89 g/cc
ASTM D297, 15
Mechanical Properties Metric English Comments
Hardness, Shore A >= 75
>= 75
ASTM D2240
80
80
Average; ASTM D2240
80
80
Dry Heat Aging 392°F; 70 hr; ASTM D865
81
81
Dry Heat Aging 392°F; 168 hr; ASTM D865
81
81
Dry Heat Aging 392°F; 336 hr; ASTM D865
Tensile Strength >= 15.4 MPa
>= 2240 psi
ASTM D412 Method A
16.0 MPa
2320 psi
Average; ASTM D412 Method A
16.5 MPa
2390 psi
Dry Heat Aging 392°F; 336 hr; ASTM D865
16.6 MPa
2410 psi
Dry Heat Aging 392°F; 168 hr; ASTM D865
17.1 MPa
2480 psi
Dry Heat Aging 392°F; 70 hr; ASTM D865
Tensile Stress 1.61 MPa

@Strain 25.0 %
233 psi

@Strain 25.0 %
Average; ASTM D412 Method A
>= 2.48 MPa

@Strain 50.0 %
>= 360 psi

@Strain 50.0 %
ASTM D412 Method A
2.56 MPa

@Strain 50.0 %
371 psi

@Strain 50.0 %
Average; ASTM D412 Method A
>= 5.45 MPa

@Strain 100 %
>= 790 psi

@Strain 100 %
ASTM D412 Method A
5.58 MPa

@Strain 100 %
810 psi

@Strain 100 %
Average; ASTM D412 Method A
Elongation at Break >= 250 %
>= 250 %
ASTM D412 Method A
260 %
260 %
Average; ASTM D412 Method A
278 %
278 %
Dry Heat Aging 392°F; 336 hr; ASTM D865
289 %
289 %
Dry Heat Aging 392°F; 168 hr; ASTM D865
296 %
296 %
Dry Heat Aging 392°F; 70 hr; ASTM D865
Modulus of Elasticity 0.009894 GPa
1.435 ksi
Calculated; ASTM D412 Method A
Shear Modulus 0.00330 GPa
0.478 ksi
Calculated; ASTM D412 Method A
Secant Modulus 0.009322 GPa
1.352 ksi
ASTM D412 Method A
Tear Strength Test 148
148
psi; ASTM D624, Die B
Compression Set 17 %

@Temperature 200 °C,
Time 79200 sec
17 %

@Temperature 392 °F,
Time 22.0 hour
ASTM D395, Test B
23 %

@Temperature 200 °C,
Time 252000 sec
23 %

@Temperature 392 °F,
Time 70.0 hour
ASTM D395, Test B
29.6 %

@Temperature 200 °C,
Time 1.21e+6 sec
29.6 %

@Temperature 392 °F,
Time 336 hour
ASTM D395, Test B
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
400 °F
Minimum Service Temperature, Air -31.1 °C
-24.0 °F
Retraction Temperature, TR10; ASTM D1329
Processing Properties Metric English Comments
Shelf Life 240 Month
240 Month
Descriptive Properties Value Comments
Strain Energy/ Unit Volume at 20% Elongation (psi) 25
ASTM D412 Method A