DuPont Performance Polymers Zytel® 70G35HSL NC010 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® 70G35HSL NC010 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass Reinforced Heat Stabilized Polyamide 66 Zytel 70G35HSL NC010 is a 35% glass fiber reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
1.41 g/cc
0.0509 lb/in³
DAM; ISO 1183
Water Absorption 5.5 %

@Thickness 2.00 mm
 5.5 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Moisture Absorption 1.70 %

@Thickness 2.00 mm
 1.70 %

@Thickness 0.0787 in
 DAM; Sim. to ISO 62
Viscosity 69000 cP

@Shear Rate 5000 1/s,
Temperature 305 °C
 69000 cP

@Shear Rate 5000 1/s,
Temperature 581 °F
 ISO 11403-1 -2
86000 cP

@Shear Rate 5000 1/s,
Temperature 295 °C
 86000 cP

@Shear Rate 5000 1/s,
Temperature 563 °F
 ISO 11403-1 -2
137000 cP

@Shear Rate 5000 1/s,
Temperature 275 °C
 137000 cP

@Shear Rate 5000 1/s,
Temperature 527 °F
 ISO 11403-1 -2
196000 cP

@Shear Rate 500 1/s,
Temperature 305 °C
 196000 cP

@Shear Rate 500 1/s,
Temperature 581 °F
 ISO 11403-1 -2
248000 cP

@Shear Rate 500 1/s,
Temperature 295 °C
 248000 cP

@Shear Rate 500 1/s,
Temperature 563 °F
 ISO 11403-1 -2
404000 cP

@Shear Rate 500 1/s,
Temperature 275 °C
 404000 cP

@Shear Rate 500 1/s,
Temperature 527 °F
 ISO 11403-1 -2
Viscosity Test 145 cm³/g
145 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Hardness, Rockwell M 89
89
50%RH; ISO 2039-2
105
105
DAM; ISO 2039-2
Hardness, Rockwell R 117
117
50%RH; ISO 2039-2
125
125
DAM; ISO 2039-2
Tensile Strength at Break 145 MPa
21000 psi
50%RH; ISO 527-1/-2
210 MPa
30500 psi
DAM; ISO 527-1/-2
Tensile Stress 7.61 MPa

@Strain 0.150 %,
Temperature 90.0 °C
 1100 psi

@Strain 0.150 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
10.92 MPa

@Strain 0.250 %,
Temperature 150 °C
 1584 psi

@Strain 0.250 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
11.43 MPa

@Strain 0.280 %,
Temperature 150 °C
 1658 psi

@Strain 0.280 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
15.04 MPa

@Strain 0.270 %,
Temperature 90.0 °C
 2181 psi

@Strain 0.270 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
19.29 MPa

@Strain 0.300 %,
Temperature 23.0 °C
 2798 psi

@Strain 0.300 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
20.06 MPa

@Strain 0.330 %,
Temperature 40.0 °C
 2909 psi

@Strain 0.330 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
39.28 MPa

@Strain 1.31 %,
Temperature 150 °C
 5697 psi

@Strain 1.31 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
47.25 MPa

@Strain 1.20 %,
Temperature 90.0 °C
 6853 psi

@Strain 1.20 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
48.84 MPa

@Strain 1.48 %,
Temperature 150 °C
 7084 psi

@Strain 1.48 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
51.17 MPa

@Strain 2.07 %,
Temperature 150 °C
 7422 psi

@Strain 2.07 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
53.63 MPa

@Strain 0.490 %,
Temperature -20.0 °C
 7778 psi

@Strain 0.490 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
55.7 MPa

@Strain 0.610 %,
Temperature 0.000 °C
 8080 psi

@Strain 0.610 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
57.58 MPa

@Strain 0.590 %,
Temperature 40.0 °C
 8351 psi

@Strain 0.590 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
59.43 MPa

@Strain 2.86 %,
Temperature 150 °C
 8620 psi

@Strain 2.86 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
64.21 MPa

@Strain 1.48 %,
Temperature 90.0 °C
 9313 psi

@Strain 1.48 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
64.53 MPa

@Strain 2.39 %,
Temperature 150 °C
 9359 psi

@Strain 2.39 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
65.31 MPa

@Strain 1.97 %,
Temperature 90.0 °C
 9472 psi

@Strain 1.97 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
65.53 MPa

@Strain 1.32 %,
Temperature 40.0 °C
 9504 psi

@Strain 1.32 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
67.63 MPa

@Strain 0.640 %,
Temperature -20.0 °C
 9809 psi

@Strain 0.640 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
69.45 MPa

@Strain 0.670 %,
Temperature 0.000 °C
 10070 psi

@Strain 0.670 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
69.61 MPa

@Strain 1.25 %,
Temperature 23.0 °C
 10100 psi

@Strain 1.25 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
75.35 MPa

@Strain 3.32 %,
Temperature 150 °C
 10930 psi

@Strain 3.32 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
77.54 MPa

@Strain 2.78 %,
Temperature 90.0 °C
 11250 psi

@Strain 2.78 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
80.8 MPa

@Strain 0.822 %,
Temperature 23.0 °C
 11700 psi

@Strain 0.822 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
85.96 MPa

@Strain 2.33 %,
Temperature 90.0 °C
 12470 psi

@Strain 2.33 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
86.61 MPa

@Strain 2.02 %,
Temperature 40.0 °C
 12560 psi

@Strain 2.02 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
89.5 MPa

@Strain 6.72 %,
Temperature 150 °C
 13000 psi

@Strain 6.72 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
95.98 MPa

@Strain 1.99 %,
Temperature 23.0 °C
 13920 psi

@Strain 1.99 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
101.06 MPa

@Strain 3.14 %,
Temperature 90.0 °C
 14658 psi

@Strain 3.14 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
101.42 MPa

@Strain 2.71 %,
Temperature 40.0 °C
 14710 psi

@Strain 2.71 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
109.93 MPa

@Strain 1.40 %,
Temperature 0.000 °C
 15944 psi

@Strain 1.40 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
114.76 MPa

@Strain 2.74 %,
Temperature 23.0 °C
 16645 psi

@Strain 2.74 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
115.13 MPa

@Strain 1.31 %,
Temperature 40.0 °C
 16698 psi

@Strain 1.31 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
118.45 MPa

@Strain 1.19 %,
Temperature 0.000 °C
 17180 psi

@Strain 1.19 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
134.55 MPa

@Strain 1.91 %,
Temperature 0.000 °C
 19515 psi

@Strain 1.91 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
136.97 MPa

@Strain 1.44 %,
Temperature -20.0 °C
 19866 psi

@Strain 1.44 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
138.77 MPa

@Strain 1.72 %,
Temperature 40.0 °C
 20127 psi

@Strain 1.72 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
146.75 MPa

@Strain 1.63 %,
Temperature 23.0 °C
 21284 psi

@Strain 1.63 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
154.33 MPa

@Strain 2.44 %,
Temperature 0.000 °C
 22384 psi

@Strain 2.44 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
157.07 MPa

@Strain 1.70 %,
Temperature 0.000 °C
 22781 psi

@Strain 1.70 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
160.1 MPa

@Strain 2.23 %,
Temperature 40.0 °C
 23220 psi

@Strain 2.23 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
167.61 MPa

@Strain 1.93 %,
Temperature -20.0 °C
 24310 psi

@Strain 1.93 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
173.95 MPa

@Strain 2.08 %,
Temperature 23.0 °C
 25229 psi

@Strain 2.08 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
174.6 MPa

@Strain 1.84 %,
Temperature -20.0 °C
 25320 psi

@Strain 1.84 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
183.67 MPa

@Strain 2.11 %,
Temperature 0.000 °C
 26639 psi

@Strain 2.11 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
190.98 MPa

@Strain 2.43 %,
Temperature -20.0 °C
 27699 psi

@Strain 2.43 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
197.12 MPa

@Strain 2.61 %,
Temperature 23.0 °C
 28590 psi

@Strain 2.61 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
Users viewing this material also viewed the following: