Sax Polymers SAXAMID 126F7 Nylon 6, 35% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Sax Polymers
Trade Name SAXAMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sax Polymers SAXAMID 126F7 Nylon 6, 35% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SAXAMID 126F7 is a polyamide 6 injection-molding-grade reinforced with 35% glass fibers. Because of its high strength and stiffness this grade is often used for stressed parts. Additional properties are very good processability and good surface quality.Information provided by SAX Polymers
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Viscosity Test 150 cm³/g
150 cm³/g
H<sub>2</sub>SO<sub>4</sub>; ISO 307
Mechanical Properties Metric English Comments
Tensile Strength 193 MPa
28000 psi
5 mm/min; ISO 527-1
Elongation at Break 4.0 %
4.0 %
5 mm/min; ISO 527-1
Tensile Modulus 10.3 GPa
1490 ksi
1 mm/min; ISO 527-1
Flexural Strength 293 MPa
42500 psi
2 mm/min; ISO 178
Flexural Modulus 8.80 GPa
1280 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
13.0 kJ/m²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO) 79.0 kJ/m²

@Temperature -30.0 °C
37.6 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1U
82.0 kJ/m²

@Temperature 23.0 °C
39.0 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
8.50 J/cm²

@Temperature 23.0 °C
40.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 209 °C
408 °F
80*10*4 s=60mm; ISO 75-1 a
Vicat Softening Point 216 °C
421 °F
B/120; ISO 306
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 °C

@Time 7200 - 21600 sec
176 °F

@Time 2.00 - 6.00 hour
Moisture Content <= 0.20 %
<= 0.20 %