Polymer Property : Tensile Strength = 28000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	193 MPa	28000 psi	Conditioned; ASTM D638
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA) (Unverified Data**) Amodel A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resistance..
Tensile Strength	193 MPa	28000 psi	50 mm/min; ISO 527
Gromax CFG45-PN11N1 Nylon 6 46% Glass Filled (Dry) Information provided by Gromax Enterprises Corp.
Tensile Strength	193 MPa	28000 psi	ASTM D638
Solvay Specialty Polymers RytonÂ® R-4-200NA Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4-200NA and R-4-200BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and low maintenance molding using conventional molding equipmentFeat..
Tensile Strength	193 MPa	28000 psi	ASTM D638
Solvay Specialty Polymers RytonÂ® XK2340 Polyphenylene Sulfide Alloy (PPS Alloy), 40% Glass Fiber RytonÂ® XK2340 40% glass fiber reinforced polyphenylene sulfide alloy compound provides excellent mechanical strength, toughness, and rigidity, along with excellent flow in thin-walled parts, low ..
Tensile Strength	193 MPa	28000 psi	5 mm/min; ISO 527-1
Sax Polymers SAXAMID 126F7 Nylon 6, 35% Glass Fiber SAXAMID 126F7 is a polyamide 6 injection-molding-grade reinforced with 35% glass fibers. Because of its high strength and stiffness this grade is often used for stressed parts. Additional properties..
Tensile Strength	193 MPa	28000 psi	ASTM D638
Solvay Specialty Polymers AmodelÂ® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned) AmodelÂ® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist..