POLYMER SEARCH

SABIC Innovative Plastics NORYL ENG265 PPE+PS

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Noryl
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics NORYL ENG265 PPE+PS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PPE+PS blend. Unfilled. Suitable for profile extrusion. NSF listed for potable water use in several colors (Standard 61). Low water absorption. Hydrolytic stability. Dimensional stability. Typical applications include tubes for reverse osmosis systems.

Physical Properties	Metric	English	Comments
Specific Gravity	1.06 g/cc	1.06 g/cc	ASTM D792
Water Absorption	0.060 % @Time 86400 sec	0.060 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	8.4 g/10 min @Load 5.00 kg, Temperature 280 °C	8.4 g/10 min @Load 11.0 lb, Temperature 536 °F	ASTM D1238
Melt Index of Compound	8.0 g/10 min @Load 5.00 kg, Temperature 280 °C	8.0 g/10 min @Load 11.0 lb, Temperature 536 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	119	119	ASTM D785
Tensile Strength at Break	50.0 MPa	7250 psi	ASTM D638
	50.0 MPa	7250 psi	ISO 527
Tensile Strength, Yield	55.0 MPa	7980 psi	ISO 527
	56.0 MPa	8120 psi	Type I, 50 mm/min; ASTM D638
Elongation at Break	27 %	27 %	ISO 527
	28 %	28 %	Type I, 50 mm/min; ASTM D638
Elongation at Yield	3.1 %	3.1 %	ISO 527
	3.3 %	3.3 %	ASTM D638
Tensile Modulus	2.40 GPa	348 ksi	5 mm/min; ASTM D638
	2.55 GPa	370 ksi	1 mm/min; ISO 527
Flexural Strength	95.0 MPa	13800 psi	ISO 178
Flexural Yield Strength	88.0 MPa	12800 psi	2.6 mm/min, 100 mm span; ASTM D790
	89.0 MPa	12900 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.45 GPa	355 ksi	2.6 mm/min, 100 mm span; ASTM D790
	2.50 GPa	363 ksi	ISO 178
	2.55 GPa	370 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	1.86 J/cm	3.48 ft-lb/in	ASTM D256
	1.14 J/cm @Temperature -30.0 °C	2.14 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	13.0 kJ/m²	6.19 ft-lb/in²	80104; ISO 180/1A
	8.00 kJ/m² @Temperature -30.0 °C	3.81 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Charpy Impact, Notched	1.30 J/cm²	6.19 ft-lb/in²	ISO 179/2C
	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	ISO 179/2C
Gardner Impact	5.00 J @Temperature -40.0 °C	3.69 ft-lb @Temperature -40.0 °F	ASTM D3029
	25.0 J @Temperature -30.0 °C	18.4 ft-lb @Temperature -22.0 °F	ASTM D3029
Dart Drop, Total Energy	39.0 J @Temperature 23.0 °C	28.8 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	59.4 µm/m-°C @Temperature -40.0 - 95.0 °C	33.0 µin/in-°F @Temperature -40.0 - 203 °F	ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)	132 °C @Thickness 3.20 mm	270 °F @Thickness 0.126 in	unannealed; ASTM D648
	137 °C @Thickness 6.40 mm	279 °F @Thickness 0.252 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	118 °C @Thickness 3.20 mm	244 °F @Thickness 0.126 in	unannealed; ASTM D648
	126 °C @Thickness 6.40 mm	259 °F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	137 °C	279 °F	Rate B/50; ISO 306
	141 °C	286 °F	Rate B/120; ISO 306
UL RTI, Electrical	105 °C	221 °F	UL 746B
UL RTI, Mechanical with Impact	90.0 °C	194 °F	UL 746B
UL RTI, Mechanical without Impact	105 °C	221 °F	UL 746B
Flammability, UL94	HB @Thickness 1.47 mm	HB @Thickness 0.0579 in	UL 94

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.65 @Frequency 50.0 - 60.0 Hz	2.65 @Frequency 50.0 - 60.0 Hz	ASTM D150
Dielectric Strength	19.6 kV/mm @Thickness 3.20 mm	498 kV/in @Thickness 0.126 in	in oil; ASTM D149
Dissipation Factor	0.00040 @Frequency 50.0 - 60.0 Hz	0.00040 @Frequency 50.0 - 60.0 Hz	ASTM D150
Arc Resistance	0.00 - 60 sec	0.00 - 60 sec	Tungsten; ASTM D495
Comparative Tracking Index	175 - 250 V	175 - 250 V	UL 746A
Hot Wire Ignition, HWI	30 - 60 sec	30 - 60 sec	UL 746A
High Amp Arc Ignition, HAI	>= 120 arcs	>= 120 arcs	UL 746A
High Voltage Arc-Tracking Rate, HVTR	>= 150 mm/min	>= 5.91 in/min	UL 746A