SABIC Innovative Plastics Lexan® FL2000 PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Lexan®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Lexan® FL2000 PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Lexan FL2000 is a medium flow specialty polycarbonate (PC) resin for structural foam molding, allowing for various weight reductions at 0.24"" (6.0mm) wall. This product offers low temperature impact strength and high heat resistance in combination with Lexan FL2000 resin is available in opaque colors only.

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	foam molded; ASTM D792
	1.21 g/cc	1.21 g/cc	ASTM D792
Water Absorption	0.13 % @Time 86400 sec	0.13 % @Time 24.0 hour	ASTM D570
Moisture Absorption at Equilibrium	0.34 %	0.34 %	ASTM D570
Linear Mold Shrinkage, Flow	0.0060 - 0.0080 cm/cm @Thickness 6.40 mm	0.0060 - 0.0080 in/in @Thickness 0.252 in	SABIC Method
Melt Flow	10.3 g/10 min @Load 1.20 kg, Temperature 300 °C	10.3 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	53.0 MPa @Thickness 6.35 mm	7690 psi @Thickness 0.250 in	ASTM D638
Elongation at Break	7.8 % @Thickness 6.35 mm	7.8 % @Thickness 0.250 in	ASTM D638
Tensile Modulus	2.30 GPa @Thickness 6.40 mm	334 ksi @Thickness 0.252 in	ASTM D638
Flexural Yield Strength	75.0 MPa	10900 psi	6.4 mm; ASTM D790
Flexural Modulus	1.93 GPa	280 ksi	6.4 mm; ASTM D790
Izod Impact, Unnotched	26.7 J/cm @Thickness 6.40 mm	50.0 ft-lb/in @Thickness 0.252 in	ASTM D4812
Dart Drop, Total Energy	122 J	90.0 ft-lb	SABIC Method
	8.00 J @Temperature -40.0 °C	5.90 ft-lb @Temperature -40.0 °F	ASTM D3763
	67.0 J @Temperature -20.0 °C	49.4 ft-lb @Temperature -4.00 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	55.8 µm/m-°C @Temperature -40.0 - 95.0 °C	31.0 µin/in-°F @Temperature -40.0 - 203 °F	ASTM E 831
Specific Heat Capacity	1.18 J/g-°C	0.282 BTU/lb-°F	ASTM C351
Deflection Temperature at 0.46 MPa (66 psi)	137 °C @Thickness 6.40 mm	279 °F @Thickness 0.252 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	126 °C @Thickness 6.40 mm	259 °F @Thickness 0.252 in	unannealed; ASTM D648
UL RTI, Electrical	80.0 °C	176 °F	UL 746B
UL RTI, Mechanical with Impact	80.0 °C	176 °F	UL 746B
UL RTI, Mechanical without Impact	80.0 °C	176 °F	UL 746B
Flammability, UL94	HB @Thickness 3.91 mm	HB @Thickness 0.154 in	UL 94
	V-1 @Thickness 5.99 mm	V-1 @Thickness 0.236 in	UL 94
Oxygen Index	28.2 %	28.2 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.60e+16 ohm-cm	3.60e+16 ohm-cm	ASTM D257
Surface Resistance	>= 1.10e+17 ohm	>= 1.10e+17 ohm	ASTM D257
Dielectric Constant	2.47 @Frequency 100 Hz	2.47 @Frequency 100 Hz	ASTM D150
	2.68 @Frequency 1.00e+6 Hz	2.68 @Frequency 1.00e+6 Hz	ASTM D150
Dissipation Factor	0.0037 @Frequency 100 Hz	0.0037 @Frequency 100 Hz	ASTM D150
	0.0039 @Frequency 1.00e+6 Hz	0.0039 @Frequency 1.00e+6 Hz	ASTM D150
Arc Resistance	60 - 120 sec	60 - 120 sec	Tungsten; ASTM D495
Comparative Tracking Index	100 - 175 V	100 - 175 V	UL 746A
Hot Wire Ignition, HWI	>= 120 sec	>= 120 sec	UL 746A
High Amp Arc Ignition, HAI	>= 120 arcs	>= 120 arcs	UL 746A
High Voltage Arc-Tracking Rate, HVTR	80.0 - 150 mm/min	3.15 - 5.91 in/min	UL 746A

Descriptive Properties	Value	Comments
FOAM - ELECTRICAL 6.4 mm Wt Reduction	20%
FOAM - Flame Class Minimum Density	0.94g/cm^3
FOAM - IMPACT 6.4 mm Wt Reduction	10%
FOAM - MECHANICAL 6.4 mm Wt Reduction	10%
FOAM - PHYSICAL 6.4mm Wt Reduction	10%
FOAM - THERMAL 6.4mm Wt Reduction	10%