SABIC Innovative Plastics LNP LUBRICOMP ZI001 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ZI001 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP ZI001 is a compound based on PPE+PS resin containing 2% Silicone. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 |
| 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
| 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 35.7 % | 35.7 % | Type I, 5 mm/min; ASTM D638 |
| 44.7 % | 44.7 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 |
| 2.50 GPa | 363 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 72.0 MPa | 10400 psi | ISO 178 |
| Flexural Modulus | 2.38 GPa | 345 ksi | 2 mm/min; ISO 178 |
| 2.52 GPa | 365 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.55 J/cm | 2.90 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.7 J/cm | 29.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 135 kJ/m² | 64.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EX1332T PC (Europe-Africa-Middle East)
- Ravago Manufacturing Americas Hylex® P1310G20 HB Polycarbonate, 20% Fiberglass Reinforced, UV Stabilized
- Mid-Mountain Materials HYTEX® 1400 Fiberglass Industrial Textile
- Multibase Multi-ABS 802 Natural Extrusion Grade
- Solvay TECHNYL® A 218W V30 Black FA PA66, 30% glass fiber, DRY
- Techmer ES Plaslube® J-50/10/SI/2 Polycarbonate, 10% GFR, 2% Silicone
- A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer
- Arlon 0.008" (0.2032 mm) Primerless Thermabond® Uncured Silicone (99990A008)
- BASF Glyoxal 40%
- Arlon Thermabond® T-20 NP (99770W015) 0.015" (0.381 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
Copyright © lookpolymers.com All Rights Reserved