A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer

Category Polymer , Thermoplastic , Ionomer , Ionomer, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and low stiffness. ApplicationFormion® FI 105 is targeted for non painted, mold-in-color, exterior or interior appearance applications requiring high or low gloss, and excellent colorability or transparency.Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 0.940 g/cc
0.940 g/cc
ISO 1183/1
Linear Mold Shrinkage 0.0060 - 0.018 cm/cm

@Thickness 3.20 mm
0.0060 - 0.018 in/in

@Thickness 0.126 in
72 hr; ISO 294
Melt Index of Compound 6.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Cond. E; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
15 sec delay; ISO 868
Tensile Strength, Ultimate 21.0 MPa
3050 psi
at max load; ISO 527
Elongation at Break 375 %
375 %
ISO 527
Flexural Modulus 0.250 GPa
36.3 ksi
Tangent; ISO 178
Izod Impact, Notched (ISO) NB
NB
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 39.0 °C

@Thickness 3.20 mm
102 °F

@Thickness 0.126 in
ISO 75
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified