Material Notes:

LNP* LUBRICOMP* UAL22S is a compound based on Polyphthalamide resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant, Heat Stabilized.

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/inÂ³	ASTM D792
	1.27 g/cc	0.0459 lb/inÂ³	ISO 1183
Moisture Absorption	0.400 %	0.400 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0087 cm/cm @Time 86400 sec	0.0087 in/in @Time 24.0 hour	ISO 294
	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.012 - 0.014 cm/cm @Time 86400 sec	0.012 - 0.014 in/in @Time 24.0 hour	ASTM D955
	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	73.0 MPa	10600 psi	ASTM D638
	74.0 MPa	10700 psi	ISO 527
Tensile Strength, Yield	73.0 MPa	10600 psi	ASTM D638
	74.0 MPa	10700 psi	ISO 527
Elongation at Break	2.5 %	2.5 %	ISO 527
	2.7 %	2.7 %	ASTM D638
Elongation at Yield	2.5 %	2.5 %	ISO 527
	2.7 %	2.7 %	ASTM D638
Tensile Modulus	3.44 GPa	499 ksi	50 mm/min; ASTM D638
	4.00 GPa	580 ksi	1 mm/min; ISO 527
Flexural Strength	110 MPa	16000 psi	ASTM D790
	122 MPa	17700 psi	ISO 178
Flexural Modulus	3.44 GPa	499 ksi	ASTM D790
	3.70 GPa	537 ksi	ISO 178
Izod Impact, Notched	0.260 J/cm	0.487 ft-lb/in	ASTM D256
Izod Impact, Unnotched	1.70 J/cm	3.18 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	2.00 kJ/mÂ²	0.952 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	17.0 kJ/mÂ²	8.09 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	5.00 J	3.69 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Coefficient of Friction, Dynamic	0.25	0.25	ASTM D3702 Modified
Coefficient of Friction, Static	0.17	0.17	ASTM D3702 Modified
K (wear) Factor	20.1 x 10^-8 mmÂ³/N-M	10.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	55.8 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	31.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	56.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	31.1 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	52.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	28.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	52.2 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	29.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)	239 Â°C	462 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	256 Â°C @Thickness 3.20 mm	493 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	136 Â°C	277 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	137 Â°C @Thickness 3.20 mm	279 Â°F @Thickness 0.126 in	unannealed; ASTM D648