Polymer Property : Linear Mold Shrinkage, Transverse = 0.014 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.012 - 0.014 cm/cm @Time 86400 sec	0.012 - 0.014 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 LNP* LUBRICOMP* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Transverse	0.012 - 0.014 cm/cm @Time 86400 sec	0.012 - 0.014 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 (Asia Pacific) LNP* Lubricomp* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Transverse	0.012 - 0.014 cm/cm @Time 86400 sec	0.012 - 0.014 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP UAL22S PPA LNP* LUBRICOMP* UAL22S is a compound based on Polyphthalamide resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant, Heat Stabilized.
Linear Mold Shrinkage, Transverse	0.013 - 0.014 cm/cm @Thickness 1.50 - 3.20 mm	0.013 - 0.014 in/in @Thickness 0.0591 - 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® EH7020 PBT MINERAL FILLED, METALLIZABLE
Linear Mold Shrinkage, Transverse	0.013 - 0.014 cm/cm @Thickness 1.50 - 3.20 mm	0.013 - 0.014 in/in @Thickness 0.0591 - 0.126 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® EH7020 PBT (Asia Pacific)
Linear Mold Shrinkage, Transverse	0.012 - 0.014 cm/cm @Time 86400 sec	0.012 - 0.014 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 LNP* THERMOCOMP* RF0029S is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized.
Linear Mold Shrinkage, Transverse	0.012 - 0.014 cm/cm @Time 86400 sec	0.012 - 0.014 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 (Asia Pacific) LNP* Thermocomp* RF0029S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.