SABIC Innovative Plastics LNP LUBRICOMP SFP36 PA12

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP SFP36 PA12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* SFP36 is a compound based on Nylon 12 resin containing 30% Glass Fiber 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D792
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
50% RH, 24 hrs; ASTM D570
0.220 %
0.220 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa
17000 psi
Type I, 5 mm/min; ASTM D638
129 MPa
18700 psi
5 mm/min; ISO 527
Tensile Strength, Yield 125 MPa
18100 psi
Type I, 5 mm/min; ASTM D638
129 MPa
18700 psi
5 mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5 mm/min; ISO 527
3.2 %
3.2 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.9 %
2.9 %
5 mm/min; ISO 527
3.2 %
3.2 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 9.06 GPa
1310 ksi
50 mm/min; ASTM D638
9.07 GPa
1320 ksi
1 mm/min; ISO 527
Flexural Strength 176 MPa
25500 psi
1.3 mm/min, 50 mm span; ASTM D790
191 MPa
27700 psi
ISO 178
Flexural Yield Strength 178 MPa
25800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 7.51 GPa
1090 ksi
1.3 mm/min, 50 mm span; ASTM D790
7.92 GPa
1150 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.46 J/cm
2.74 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.0 J/cm
18.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 58.0 kJ/m²
27.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 9.00 J

@Temperature 23.0 °C
 6.64 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.67
0.67
ASTM D3702 Modified
Coefficient of Friction, Static 0.52
0.52
ASTM D3702 Modified
K (wear) Factor 28.2 x 10-8 mm³/N-M
14.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 27.5 µm/m-°C

@Temperature -30.0 - 30.0 °C
 15.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 44.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 177 °C
351 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
177 °C

@Thickness 3.20 mm
 351 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 169 °C
336 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
172 °C

@Thickness 3.20 mm
 342 °F

@Thickness 0.126 in
 unannealed; ASTM D648