Polymer Property : Tensile Strength at Break = 129 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 129 MPa
18700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RX05050 PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RX05050 is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break 129 MPa
18700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP SFP36 PA12
LNP* LUBRICOMP* SFP36 is a compound based on Nylon 12 resin containing 30% Glass Fiber 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
Tensile Strength at Break 129 MPa
18700 psi
ASTM D 638
SABIC Innovative Plastics LNP Stat-kon DEL339XC PC
LNP STAT-KON* DEL339XC is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supp..
Tensile Strength at Break 129 MPa
18700 psi
ISO 527
SABIC Innovative Plastics LNP Stat-kon DEL339XC PC
LNP STAT-KON* DEL339XC is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supp..
Tensile Strength at Break 129 MPa
18700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF006 PC (Asia Pacific)
LNP* Thermocomp* DF006 is a compound based on Polycarbonate resin containing Glass Fiber.
Tensile Strength at Break 129 MPa
18700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF006 PC (Europe-Africa-Middle East)
LNP* Thermocomp* DF1006 is a compound based on Polycarbonate resin containing Glass Fiber.
Tensile Strength at Break 129 MPa
18700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF006 PA 6
LNP THERMOCOMP* PF006 is a compound based on Nylon 6 resin containing 30% Glass Fiber.
Tensile Strength at Break 129 MPa
18700 psi
ASTM D 638
SABIC Innovative Plastics LNP Stat-kon DEL339XC PC (Asia Pacific)
LNP STAT-KON* DEL339XC is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was supp..
Tensile Strength at Break 129 MPa
18700 psi
ISO 527
SABIC Innovative Plastics LNP Stat-kon DEL339XC PC (Asia Pacific)
LNP STAT-KON* DEL339XC is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was supp..
Tensile Strength at Break 129 MPa
18700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP OF006A PPS - Branched
LNP* THERMOCOMP* OF006A is a compound based on PPS - Branched resin containing 30% Glass Fiber.
Tensile Strength at Break 129 MPa
18700 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP OF006A PPS - Branched
LNP* THERMOCOMP* OF006A is a compound based on PPS - Branched resin containing 30% Glass Fiber.
Tensile Strength at Break 129 MPa
18700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6
LNP THERMOCOMP* PF006S is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 129 MPa
18700 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6
LNP THERMOCOMP* PF006U is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of thie grade are: UV Stabilized.
Tensile Strength at Break 129 MPa
18700 psi
ISO 527-1/-2
Unitika RUN35-C25 PA6, Conditioned
High modulus and low warpage nylonInformation provided by Unitika Ltd.
Tensile Strength at Break 129 MPa
18700 psi
ISO 527-1/-2
DuPont Performance Polymers Rynite® FR531 NC010 Polyethylene Terephthalate (PET)  (Unverified Data**)
36% Reinforced Flame Retardant Polyethylene Terephthalate Information provided by DuPont Performance Polymers
Tensile Strength at Break 129 MPa
18700 psi
ASTM D 638
SABIC Innovative Plastics LNP Verton NV006E PC/ABS
LNP* Verton* NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas region..
Tensile Strength at Break 129 MPa
18700 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON NV006E PC/ABS (Asia Pacific)
LNP* Verton* NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break 129 MPa
18700 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOTUF OF008I PPS - Linear (Europe-Africa-Middle East)
LNP* Thermotuf* OF008I is a compound based on PPS - Linear resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Strength at Break 129 MPa
18700 psi
ASTM D638
SABIC Innovative Plastics LNP VERTON NV006E PC+ABS
LNP* Verton* NV006E is a compound based on PC+ABS blend resin containing 30% Long Glass Fiber. Added features of this material include: Easy Molding, Structural.