Polymer Property : Flexural Yield Strength = 25800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	177.9 MPa	25800 psi	ASTM D790
Covestro Petlon® 7530 Semi-Crystalline PET, 35% Mineral/Glass Fiber (discontinued **) Characteristics: Excellent Electrical Properties, High Heat and Chemical ResistanceApplications: Automotive (Under Hood), Appliances, Casings and HousingsProcessing: Injection Molding (Melt Temperat..
Flexural Yield Strength	178 MPa	25800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Lubricomp LFL36 PEEK (Europe-Africa-Middle East) LNPLUBRICOMP LFL36 is a compound based on Polyetheretherketone resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated.This data was supplied by SABIC-IP for the Europe-A..
Flexural Yield Strength	178 MPa	25800 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP SFP36 PA12 LNP* LUBRICOMP* SFP36 is a compound based on Nylon 12 resin containing 30% Glass Fiber 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
Flexural Yield Strength	178 MPa	25800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP DF004ER PC (Europe-Africa-Middle East) LNP* Thermocomp* DF004ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Flexural Yield Strength	178 MPa	25800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding.
Flexural Yield Strength	178 MPa	25800 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP JF004Z PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004Z is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: HV.
Flexural Yield Strength	178 MPa	25800 psi	ASTM D790
Covestro Baydur® STR/C-405 IMR Polyurethane Composite SRIM Foam, 45% Glass Filled, MDI-based 2-Component Liquid System Contains continuous strand fiberglass mat.0.118 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer ..