Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 342 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
ISO 75-f
Victrex® ST™ STG45 PolyEtherKetoneEtherKetoneKetone, Unreinforced
Product Description:High performance thermoplastic material, unreinforced PolyEtherKetoneEtherKetoneKetone (PEKEKK), semi crystalline, depth filtered granules for injection moulding, standard flow, ..
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
Covestro Apec® DP 1-9379/7 Polycarbonate  (discontinued **)
Key Features:Release agentUnfilledU.V. stabilized or stable to weatherSuitable processing methods:Injection moldingThermoformingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer M..
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
ASTM D648
LATI LATILUB 95-25GR CE/10 Polysulfone Base (PSU), 25% Graphite, 10% Special Mineral Filled Self Lubricating Plastic
Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri..
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
ISO 75-1/-2
Lanxess Pocan® KU 2-7209 Z 000000 PBT, 15% Glass Fiber
PBT, 15% glass fibers, injection molding, flame retardant, impact modified
Deflection Temperature at 1.8 MPa (264 psi) 172 °C

@Thickness 3.20 mm
342 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP SFP36 PA12
LNP* LUBRICOMP* SFP36 is a compound based on Nylon 12 resin containing 30% Glass Fiber 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant.
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Ultem UR9076LG PEI
Standard flow mineral filled Polyetherimide Blend. Restricted sales to GE Specialty Film & Sheet.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP Lexan_BFL2200 PC
design for black light frame application as high flow PC, V-2, high reflection grade.
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP Lexan_BFL2200 PC (Asia Pacific)
design for black light frame application as high flow PC, V-2, high reflection grade.
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP Lexan_BFL2200 PC (Europe-Africa-Middle East)
design for black light frame application as high flow PC, V-2, high reflection grade.
Deflection Temperature at 1.8 MPa (264 psi) 172 °C

@Thickness 3.20 mm
342 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RF002ES PA 66
LNP THERMOCOMP* RF002ES is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 172 °C

@Thickness 3.20 mm
342 °F

@Thickness 0.126 in
unannealed; ASTM D 648
SABIC Innovative Plastics LNP Lubricomp KFI12A Acetal Homopolymer
LNP LUBRICOMP* KFI12A is a compound based on Acetal Homopolymer resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABI..
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-LOY WF306C PBT
LNP* STAT-LOY* WF306C is a compound based on PBT resin containing 30% Glass Fiber. Added features of this material include: Antistat, Clean Compound System.
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-LOY WF306C PBT (Asia Pacific)
LNP* Stat-loy* WF306C is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: Antistat, Clean Compounding System.
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
ISO 75-1/-2
Covestro Apec® 2097 Polycarbonate
Easy flowingeasy to demoldUV-stabilizedsoftening temperature (VST/B 120)=202 °CPreprocessingMax. Water content
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
ISO 75-1/-2
DuPont Performance Polymers Delrin® 525GR NC000 Acetal (POM)  (Unverified Data**)
25% Glass Reinforced Medium Viscosity Acetal Homopolymer Delrin 525GR NC000 is a 25% glass reinforced acetal homopolymer for injection molding. It has very high strength stiffness and high deflectio..
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
D648
Ensinger Tecapeek® ST PolyEtherKetoneEtherKetoneKetone, Unreinforced
TECAPEEK® ST is a multipurpose semi-crystaline material from the polyaryletherketone family based on PEKEKK that features improved mechanical properties at higher temperatures. The benefits of TECA..
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
ASTM D648
E-Polymers Tekaloy® T80GFR , Flame Retardant, 30% Glass Fiber Reinforced PBT/ABS Alloy
30% Glass Fiber reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd.