SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ASTM D792
	1.37 g/cc	0.0495 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
	0.0080 cm/cm @Time 86400 sec	0.0080 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0096 cm/cm @Time 86400 sec	0.0096 in/in @Time 24.0 hour	ISO 294
	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	38.0 MPa	5510 psi	ISO 527
	38.0 MPa	5510 psi	ASTM D638
Tensile Strength, Yield	42.0 MPa	6090 psi	ASTM D638
	43.0 MPa	6240 psi	ISO 527
Elongation at Break	18.2 %	18.2 %	ISO 527
	22.3 %	22.3 %	ASTM D638
Elongation at Yield	5.1 %	5.1 %	ISO 527
	5.4 %	5.4 %	ASTM D638
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
	2.58 GPa	374 ksi	1 mm/min; ISO 527
Flexural Strength	69.0 MPa	10000 psi	ISO 178
Flexural Modulus	2.40 GPa	348 ksi	ISO 178
	2.75 GPa	399 ksi	ASTM D790
Izod Impact, Notched	1.92 J/cm	3.60 ft-lb/in	ASTM D256
Izod Impact, Unnotched	15.0 J/cm	28.1 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	14.0 kJ/m²	6.66 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	105 kJ/m²	50.0 ft-lb/in²	80104; ISO 180/1U
Dart Drop, Total Energy	31.0 J	22.9 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	25.0 J	18.4 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.41	0.41	ASTM D3702 Modified
Coefficient of Friction, Static	0.48	0.48	ASTM D3702 Modified
K (wear) Factor	280 x 10^-8 mm³/N-M	139 x 10^-10 in³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	53.0 µm/m-°C @Temperature -40.0 - 40.0 °C	29.4 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
	54.0 µm/m-°C @Temperature -40.0 - 40.0 °C	30.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
CTE, linear, Transverse to Flow	59.4 µm/m-°C @Temperature -40.0 - 40.0 °C	33.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	60.0 µm/m-°C @Temperature -40.0 - 40.0 °C	33.3 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	139 °C	282 °F	Flatw 80104 sp=64mm; ISO 75/Bf
	142 °C @Thickness 3.20 mm	288 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	135 °C	275 °F	Flatw 80104 sp=64mm; ISO 75/Af
	135 °C @Thickness 3.20 mm	275 °F @Thickness 0.126 in	unannealed; ASTM D648