- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 142 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 142 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Lexan® 503RS PC (Europe-Africa-Middle East) LEXAN 503RS is a medium viscosity, glass reinforced, flame retardant grade UV stabilized grade. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp DFI12E PC (Asia Pacific) LNP* Lubricomp* DFI12E is a compound based on Polycarbonate resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated, Easy Molding.This data was suppli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Asia Pacific) LNP* Lubricomp* DL001 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp DFI12E PC LNP* Lubricomp* DFI12E is a compound based on Polycarbonate resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated, Easy Molding.This data was suppli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 4.00 mm |
288 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1200-22 Polycarbonate Resin Description: LUPOY PC 1200-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 4.00 mm |
288 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1301EP-22 Polycarbonate Resin Description: LUPOY PC 1301EP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 4.00 mm |
288 °F @Thickness 0.157 in |
Annealed; ASTM D648 |
| LG Chemical Lupoy 1303EP-22 Polycarbonate Resin Description: LUPOY PC 1303EP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 listing. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DX05305C PC (Asia Pacific) LNP* Stat-kon* DX05305C is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DX98477 PC LNP* STAT-KON* DX98477 is a compound based on Polycarbonate containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC (Asia Pacific) LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP DF0079 PC (Europe-Africa-Middle East) LNP* Thermocomp* DF0079 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® GW-3130 PC, 10% Glass Filled Recycled Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® GW-3130 PC, 10% Glass Filled Recycled Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 6.40 mm |
288 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® HN-3102G PC, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Unannealed; ISO 75-2/B |
| Styron CALIBREâ„¢ 201-22 Polycarbonate Resin Overview: CALIBREâ„¢ 201-22 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistanc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Unannealed; ISO 75-2/B |
| Styron CALIBREâ„¢ 203-22 Polycarbonate Resin Overview: CALIBREâ„¢ 200-22 polycarbonate resins are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistanc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | annealed; ASTM D648 |
| Styron CALIBREâ„¢ 2061-22 Polycarbonate CALIBREâ„¢ 2061-22 resin is used in applications involving steam or ethylene oxide for sterilization - though suitability for use in these applications is dependent upon autoclave cycle times and.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Annealed; ISO 75-2/B |
| Styron CALIBREâ„¢ 301EP-22 Polycarbonate Resin Overview: CALIBREâ„¢ 300EP-22 Series are polycarbonate resins that offer exceptional impact resistance, heat distortion resistance and optical clarity for injection molding applications. Their hi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | 0.157 in, annealed; ASTM D648 |
| Styron EMERGEâ„¢ 4330-22 Polycarbonate EMERGEâ„¢ PC 4330-22 advanced resin is high-performance polycarbonate resin offering ultraviolet light stability, high heat resistance, toughness, and superior flow. Applications: Consumer Elec.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | 0.157 in, annealed; ASTM D648 |
| Styron EMERGEâ„¢ 4510-6 Polycarbonate EMERGEâ„¢ PC 4510-6 advanced resin is a general purpose polycarbonate resin offering ignition resistance, heat resistance and excellent toughness. Applications: Consumer Electronics and Informa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | Annealed; ISO 75-2/B; ASTM D648 |
| Styron CALIBREâ„¢ 302EP-22 Polycarbonate Resin Overview: CALIBREâ„¢ 300EP-22 Series are polycarbonate resins that offer exceptional impact resistance, heat distortion resistance and optical clarity for injection molding applications. Their hi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ISO 75 |
| Teijin Panlite® LV-2250Z Transparent and Weather Resistant grade Polycarbonate Resin Typical injection molding grade that has weather resistance and is bluish-tinted to exhibit clear color.Applications:Components of electric, electronic, business machine and industrial equipment com.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 234 is an injection molding grade, 20% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance, high stiffness and lo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ASTM D648 |
| Plastics Group Polifil® GFPP-20 20% Glass-Reinforced Polypropylene Polifil® GFPP series compounds are homopolymer polypropylene resins reinforced with glass fibers. They provide high impact with increased strength, stiffness, surface hardness, and higher continuou.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | |
| Covestro Makrolon® 9125 Polycarbonate Medium viscosity, flame retardant extrusion and injection molding grade with 20% standard glass fibers and easy mold release agent.Information provided by Bayer.As of 1 September 2015, Bayer Materia.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ISO 75-1/-2 |
| Covestro Makrolon® 9415 Polycarbonate, 10% Glass Filled ISO 7391-PC,MFR,(,,)-09-9,GF10Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 min10 % Glass fiber reinforcedChlorine- and bromine-free flame retardantUL 94V-0/1.5 mm and 5VA/3.0 mmHigh viscosityEasy rel.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 500TE NC010 Acetal (POM)
(Unverified Data**) Toughened Medium Viscosity Acetal Homopolymer with Very Low Emissions Delrin 500TE NC010 (formerly DE20560) is a medium viscosity toughened acetal homopolymer with very low VOC emissions. Processing.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ASTM D648 |
| ExxonMobil Exxtral™ MDK340 Performance Polyolefin Product Description: A medium melt flow rate, 40% mineral-filled polyolefin resin suitable for injection molded consumer products and appliance applications requiring long-term heat ageing resistanc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 288 °F | ISO 75 |
| Teijin Panlite® G-3410H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin Reinforced with 10 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPreci.. |
|||