SABIC Innovative Plastics LNP LUBRICOMP OCP34E PPS - Linear

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP OCP34E PPS - Linear.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* OCP34E is a compound based on PPS - Linear resin containing 20% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Easy Molding, Electrically Conductive, Wear Resistant.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
1.46 g/cc
0.0527 lb/in³
ISO 1183
Moisture Absorption 0.0200 %
0.0200 %
50% RH, 24 hrs; ASTM D570
0.0200 %
0.0200 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.00080 cm/cm

@Time 86400 sec
0.00080 in/in

@Time 24.0 hour
ISO 294
0.0010 cm/cm

@Time 86400 sec
0.0010 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0039 cm/cm

@Time 86400 sec
0.0039 in/in

@Time 24.0 hour
ISO 294
0.0040 cm/cm

@Time 86400 sec
0.0040 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 159 MPa
23100 psi
ISO 527
164 MPa
23800 psi
ASTM D638
Elongation at Break 1.3 %
1.3 %
ISO 527
1.6 %
1.6 %
ASTM D638
Tensile Modulus 16.59 GPa
2406 ksi
1 mm/min; ISO 527
18.96 GPa
2750 ksi
50 mm/min; ASTM D638
Flexural Strength 231 MPa
33500 psi
ASTM D790
236 MPa
34200 psi
ISO 178
Flexural Modulus 14.96 GPa
2170 ksi
ASTM D790
15.32 GPa
2222 ksi
ISO 178
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.89 J/cm
7.29 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 28.0 kJ/m²
13.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J
2.95 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
265 °C

@Thickness 3.20 mm
509 °F

@Thickness 0.126 in
unannealed; ASTM D648