SABIC Innovative Plastics GELOY HRA222F ASA+PC

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY HRA222F ASA+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Geloy HRA222F is a multi-purpose, chlorine and bromine free flame retardant PC+ASA alloy for injection molding processes. F1 rating according UL746C. Use for exterior/interior electrical applications requiring UV resistance.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 13 g/10 min

@Load 2.16 kg,
Temperature 260 °C
13 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
50 mm/min; ISO 527
51.0 MPa
7400 psi
5 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D638
66.0 MPa
9570 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 59.0 MPa
8560 psi
Type I, 5 mm/min; ASTM D638
60.0 MPa
8700 psi
50 mm/min; ISO 527
62.0 MPa
8990 psi
5 mm/min; ISO 527
63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break >= 50 %
>= 50 %
5 mm/min; ISO 527
>= 50 %
>= 50 %
50 mm/min; ISO 527
>= 100 %
>= 100 %
Type I, 50 mm/min; ASTM D638
>= 100 %
>= 100 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 4.2 %
4.2 %
Type I, 5 mm/min; ASTM D638
4.3 %
4.3 %
5 mm/min; ISO 527
4.3 %
4.3 %
Type I, 50 mm/min; ASTM D638
4.4 %
4.4 %
50 mm/min; ISO 527
Tensile Modulus 2.52 GPa
365 ksi
1 mm/min; ISO 527
2.59 GPa
376 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 93.0 MPa
13500 psi
2 mm/min; ISO 178
Flexural Modulus 2.51 GPa
364 ksi
2 mm/min; ISO 178
Izod Impact, Notched 3.85 J/cm
7.21 ft-lb/in
ASTM D256
2.90 J/cm

@Temperature 0.000 °C
5.43 ft-lb/in

@Temperature 32.0 °F
ASTM D256
Izod Impact, Notched (ISO) 17.0 kJ/m²
8.09 ft-lb/in²
80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
12.0 kJ/m²

@Temperature 0.000 °C
5.71 ft-lb/in²

@Temperature 32.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
38.3 µin/in-°F

@Temperature -22.0 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 71.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
39.4 µin/in-°F

@Temperature -22.0 - 176 °F
ISO 11359-2
75.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
41.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 99.0 °C
210 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 102 °C
216 °F
Rate B/50; ISO 306
104 °C
219 °F
Rate B/120; ISO 306
111 °C
232 °F
Rate A/50; ISO 306
UL RTI, Electrical 90.0 °C
194 °F
UL 746B
UL RTI, Mechanical with Impact 90.0 °C
194 °F
UL 746B
UL RTI, Mechanical without Impact 90.0 °C
194 °F
UL 746B
Flammability, UL94 V-0

@Thickness 2.00 mm
V-0

@Thickness 0.0787 in
UL 94
Oxygen Index 29 %
29 %
ISO 4589
Electrical Properties Metric English Comments
Comparative Tracking Index >= 600 V
>= 600 V
UL 746A
600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2
UV-light, water exposure/immersion F1
UL 746C