SABIC Innovative Plastics Cycoloy® CE1810 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CE1810 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D 792
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.050 %
0.050 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %

@Temperature 23.0 °C
0.20 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 6.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
6.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
7.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
7.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D 1238
24 g/10 min

@Load 5.00 kg,
Temperature 300 °C
24 g/10 min

@Load 11.0 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
Type I, 5 mm/min; ASTM D 638
45.0 MPa
6530 psi
5 mm/min; ISO 527
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 5 mm/min; ASTM D 638
60.0 MPa
8700 psi
5 mm/min; ISO 527
Elongation at Break 15 %
15 %
Type I, 5 mm/min; ASTM D 638
15 %
15 %
5 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 5 mm/min; ASTM D 638
4.0 %
4.0 %
5 mm/min; ISO 527
Tensile Modulus 4.65 GPa
674 ksi
5 mm/min; ASTM D 638
4.65 GPa
674 ksi
1 mm/min; ISO 527
Flexural Yield Strength 105 MPa
15200 psi
1.3 mm/min, 50 mm span; ASTM D 790
105 MPa
15200 psi
2 mm/min; ISO 178
Flexural Modulus 4.45 GPa
645 ksi
1.3 mm/min, 50 mm span; ASTM D 790
4.45 GPa
645 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.900 J/cm

@Temperature -30.0 °C
1.69 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
1.70 J/cm

@Temperature 23.0 °C
3.18 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
20.0 kJ/m²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Impact Test 60.0 J

@Temperature 23.0 °C
44.3 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 43.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
43.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 59.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
32.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
59.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
32.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
121 °C

@Thickness 3.20 mm
250 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 139 °C
282 °F
Rate B/50; ASTM D 1525
139 °C
282 °F
Rate B/50; ISO 306
141 °C
286 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2