Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 4.65 GPa | 674 ksi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne LubriOne™ NY-10GF/10T BLACK Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® CE1810 PC+ABS (Asia Pacific) PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CE1810 PC+ABS (Asia Pacific) PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® CE1810 PC+ABS (Europe-Africa-Middle East) PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CE1810 PC+ABS (Europe-Africa-Middle East) PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS Reinforced PC/ABS with high stiffness and low CTE. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS Reinforced PC/ABS with high stiffness and low CTE. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS (Asia Pacific) Reinforced PC/ABS with high stiffness and low CTE. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS (Asia Pacific) Reinforced PC/ABS with high stiffness and low CTE. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS (Europe-Africa-Middle East) Reinforced PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS (Europe-Africa-Middle East) Reinforced PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Modulus | 4.65 GPa | 675 ksi | ASTM D638 |
Quadrant EPP Nylatron® GF30 Nylon Type 66, 30% Glass-Reinforced Black Color (ASTM Product Data Sheet) |
|||
Tensile Modulus | 4.65 GPa | 675 ksi | ASTM D638 |
Fiberfil® M-1812 Polypropylene Homopolymer, 45% Talc Filled Information provided by FIBERFIL Engineered Plastics |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL RN1300 PPE (Asia Pacific) 15% glass/mineral reinforced PPE. Nonchlorinated, nonbrominated, flame-retardant. Black and gray. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP WX05456 Polyester, TP LNP THERMOCOMP* WX05456 is a compound based on Polyester, TP resin containing Mineral. |
|||
Tensile Modulus | 4.65 GPa | 675 ksi | ASTM D638 |
Ensinger DELRIN® 570 Acetal, 20% Glass Filled (POM) DELRIN®570 Shapes manufactured by Ensinger are 20% glass filled materials intended for general industrial use. The material offers very high stiffness, low warpage, and low creep for superior part .. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® CE1810 PC+ABS PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Modulus | 4.65 GPa | 674 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® CE1810 PC+ABS PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Americas region. |