SABIC Innovative Plastics Geloy XTPM302 ASA+PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Geloy XTPM302 ASA+PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
XTPM302 is a general purpose ASA/PC injection moulding grade, available in various colors.Typical properties measured on natural material.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.30 %
0.30 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.80 %

@Temperature 23.0 °C
0.80 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
on tensile bar; SABIC Method
Melt Flow 10 g/10 min

@Load 10.0 kg,
Temperature 220 °C
10 g/10 min

@Load 22.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
10 g/10 min

@Load 5.00 kg,
Temperature 240 °C
10 g/10 min

@Load 11.0 lb,
Temperature 464 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
27 g/10 min

@Load 5.00 kg,
Temperature 260 °C
27 g/10 min

@Load 11.0 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa
6240 psi
50 mm/min; ISO 527
43.0 MPa
6240 psi
5 mm/min; ISO 527
44.0 MPa
6380 psi
Type I, 50 mm/min; ASTM D 638
47.0 MPa
6820 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 49.0 MPa
7110 psi
5 mm/min; ISO 527
51.0 MPa
7400 psi
Type I, 5 mm/min; ASTM D 638
54.0 MPa
7830 psi
50 mm/min; ISO 527
55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 55 %
55 %
50 mm/min; ISO 527
80 %
80 %
5 mm/min; ISO 527
95 %
95 %
Type I, 50 mm/min; ASTM D 638
>= 100 %
>= 100 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 3.3 %
3.3 %
5 mm/min; ISO 527
3.6 %
3.6 %
Type I, 5 mm/min; ASTM D 638
3.7 %
3.7 %
Type I, 50 mm/min; ASTM D 638
3.7 %
3.7 %
50 mm/min; ISO 527
Tensile Modulus 2.37 GPa
344 ksi
1 mm/min; ISO 527
2.37 GPa
344 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.05 J/cm

@Temperature -30.0 °C
1.97 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
1.40 J/cm

@Temperature -20.0 °C
2.62 ft-lb/in

@Temperature -4.00 °F
ASTM D 256
1.75 J/cm

@Temperature -10.0 °C
3.28 ft-lb/in

@Temperature 14.0 °F
ASTM D 256
2.85 J/cm

@Temperature 0.000 °C
5.34 ft-lb/in

@Temperature 32.0 °F
ASTM D 256
4.85 J/cm

@Temperature 23.0 °C
9.09 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -20.0 °C
3.33 ft-lb/in²

@Temperature -4.00 °F
80*10*4; ISO 180/1A
11.0 kJ/m²

@Temperature -10.0 °C
5.23 ft-lb/in²

@Temperature 14.0 °F
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature 0.000 °C
7.14 ft-lb/in²

@Temperature 32.0 °F
80*10*4; ISO 180/1A
28.0 kJ/m²

@Temperature 23.0 °C
13.3 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
3.80 J/cm²

@Temperature 23.0 °C
18.1 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 94.0 J
69.3 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Hot Ball Pressure Test <= 100 °C
<= 212 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 103 °C
217 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 103 °C
217 °F
Rate B/50; ISO 306
104 °C
219 °F
Rate B/120; ISO 306
116 °C
241 °F
Rate A/50; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity 2.50e+15 ohm-cm
2.50e+15 ohm-cm
ASTM D 257
Surface Resistance 1.90e+16 ohm
1.90e+16 ohm
ASTM D 257
Dielectric Strength 27.8 kV/mm

@Thickness 1.60 mm
706 kV/in

@Thickness 0.0630 in
in oil; ASTM D 149
Dissipation Factor 0.0175

@Frequency 1.00e+6 Hz
0.0175

@Frequency 1.00e+6 Hz
ASTM D 150