Polyram PlusTek PD1002NT Nylon 12 for Extrusion
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Extrusion/Tubing Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PD1002NT Nylon 12 for Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Medium viscosity Nylon 12 for extrusion application.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.15 % | 1.15 % | ISO 62 |
| Linear Mold Shrinkage | 0.0080 - 0.0090 cm/cm | 0.0080 - 0.0090 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
| Elongation at Break | 70 % | 70 % | ISO 527 |
| Tensile Modulus | 1.10 GPa | 160 ksi | ISO 527 |
| Izod Impact, Unnotched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 175 °C | 347 °F | ISO 11357 |
| Maximum Service Temperature, Air | 105 °C | 221 °F | Continuous use |
| 150 °C | 302 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- Fiberfil® PP-60/TC/10 Polypropylene Homopolymer, 10% Talc Filled
- Kinlead PP11 Printing Grade BOPP Plain Film (thickness: 20 µm)
- Indium Corp. Indalloy® 7 In-Pb Solder Alloy
- Gromax BFG30-EN03N1 Nylon 6 33% Glass Filled (Dry)
- Master Bond EP21SC-1 Two Component Epoxy Resin System
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.0 PHR Di-Cup 40C Peroxide
- China Tungsten YG8X Tungsten Carbide
- AK Steel ASTM A 907, Grade 33 Hot Rolled Carbon Steel, Structural Quality (SQ)
- Borealis Borsoft™ SG220MO Polypropylene Random Copolymer for Injection Molding
- Polyram PlusTek RB506 Nylon 6, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved