Gromax BFG30-EN03N1 Nylon 6 33% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG30-EN03N1 Nylon 6 33% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ISO 1183 |
| Moisture Absorption | 0.850 % | 0.850 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Temperature 80.0 °C |
0.0030 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Temperature 80.0 °C |
0.0060 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 91 | 91 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 132 MPa | 19200 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 2.6 % | 2.6 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 7.20 GPa | 1040 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 215 MPa | 31200 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 8.63 GPa | 1250 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 5.30 J/cm² @Temperature 23.0 °C |
25.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 0.720 J/cm² @Temperature 23.0 °C |
3.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Gwent Electronic Materials C2020322D6 Platinum Polymeric Ink
- SABIC Innovative Plastics LNP Lubricomp UX06442 PPA (Asia Pacific)
- Plenco 4504 Phenolic, Granular, Injection Molded
- Epoxy Technology EPO-TEK® CF6-2 High Temperature Epoxy
- Covestro Bayblend® T 88-2N Polycarbonate/ABS Blend, 10% Glass Fiber
- ExxonMobil Santoprene® 121-80 Thermoplastic Elastomer
- 3M 9472FL Adhesive Transfer Tape with 300LSE Adhesive
- Colorite Polymers Weatherflex™ CS7524WX (NTL01P) Wire and Cable Vinyl Compound
- A. Schulman ComAlloy Hiloy® 627 Nylon 6/6, Mineral Reinforced
- E-Polymers TEKALOY® F50G30 30% Glass Fiber Reinforced PBT/PET Alloy
Copyright © lookpolymers.com All Rights Reserved