Polymer Resources PC-G10-[color]-1 Polycarbonate, 10% Glass Reinforced with Mold Release
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC-G10-[color]-1 Polycarbonate, 10% Glass Reinforced with Mold Release.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, 10% Glass Reinforced with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 5.0 - 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 |
| Tensile Strength, Yield | 62.7 MPa | 9100 psi | ASTM D638 |
| Flexural Strength | 109 MPa | 15800 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.70 mm |
V-2 @Thickness 0.0669 in |
|
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 293 - 316 °C | 560 - 600 °F | |
| Middle Barrel Temperature | 304 - 327 °C | 580 - 620 °F | |
| Front Barrel Temperature | 316 - 338 °C | 600 - 640 °F | |
| Melt Temperature | 302 - 329 °C | 575 - 625 °F | |
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |
| Drying Temperature | 118 - 124 °C | 245 - 255 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Echo® RPEHD NAT Recycled HDPE
- Meilian Chemical PE42095 YELLOW MASTERBATCH
- Karina E 1000/00851-IE White MBPEB Color Concentrate
- SCG Chemicals EL-Proâ„¢ P440J Polypropylene Injection Molding
- A. Schulman POLYBATCH™ Blue 4500GZ Concentrate Based in Low-Density Polyethylene
- Diamond Polymers ASA S519
- Fainplast Compounds HL 101 Flexible PVC, Insulation for High Temperatures
- ChevronTexaco Doro® AR SAE 30
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR N220 (ISAF) Filler
Copyright © lookpolymers.com All Rights Reserved