- Polykemi AB POLYblend 45FS GK25 PC/ABS-Blend, Glass Fiber reinforced
Polykemi AB POLYblend 45FS GK25 PC/ABS-Blend, Glass Fiber reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | Polykemi AB |
| Trade Name | POLYblend |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYblend 45FS GK25 PC/ABS-Blend, Glass Fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Filler Content | 25 % | 25 % | ±2%; Polykemi |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 27.0 MPa | <= 3920 psi | ISO/R527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 57.0 MPa | <= 8270 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| 0.300 J/cm² @Temperature -20.0 °C |
1.43 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 100 °C @Load 5.001 kg |
212 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 108 °C @Load 1.00 kg |
226 °F @Load 2.21 lb |
50°C/h; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Dry Time | 2 - 8 hour | 2 - 8 hour | in circulation dryer |
| 2 - 8 hour | 2 - 8 hour | in fresh-air dryer | |
| 2 - 8 hour | 2 - 8 hour | in desiccant air dryer | |
| Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-50 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible 90048 Polyvinyl Chloride, Flexible (PVC, Flexible)
- ExxonMobil Escorene® MV 02514 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
- Akro-Plastic Akromid® B3 3 S3 10 PA, Dry-Impact Resistant (Unverified Data**)
- Solvay TECHNYL® A 218 V30 Black 21 NHFE PA66, 30% glass fiber, DRY
- Techmer ES Elastoblend® PA6 IM X
- Unifrax Fiberfrax® 7001-F-5 High Purity Bulk Fiber
- ExxonMobil SAE 30 Mobilgard ADL Series
- ExxonMobil Jayflex™ DIUP Plasticizer (European Grade)
- Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), unnotched
Copyright © lookpolymers.com All Rights Reserved