PolyOne LubriOne™ NJ-30CF/15T-2S Nylon 12 (discontinued **)

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne LubriOne™ NJ-30CF/15T-2S Nylon 12 (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.

Physical Properties	Metric	English	Comments
Specific Gravity	1.27 g/cc	1.27 g/cc	ASTM D792
Water Absorption	0.10 % @Time 86400 sec	0.10 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.00020 - 0.0010 cm/cm	0.00020 - 0.0010 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.010 - 0.020 cm/cm	0.010 - 0.020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	121 MPa	17500 psi	Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield	121 MPa	17500 psi	ASTM D638
Elongation at Break	4.1 %	4.1 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	16.5 GPa	2390 ksi	ASTM D638
Flexural Strength	190 MPa	27600 psi	ASTM D790
Flexural Modulus	10.7 GPa	1550 ksi	ASTM D790
Izod Impact, Notched	1.44 J/cm @Thickness 6.35 mm, Temperature 23.0 °C	2.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Coefficient of Friction, Dynamic	0.13	0.13	vs. Steel; ASTM D1894
Coefficient of Friction, Static	0.24	0.24	vs. Steel; ASTM D1894

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	176 °C	349 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	166 °C	331 °F	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	100 - 10000 ohm-cm	100 - 10000 ohm-cm	ASTM D257
Surface Resistance	100 - 10000 ohm	100 - 10000 ohm	ASTM D257

Processing Properties	Metric	English	Comments
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	71.1 - 82.2 °C @Time 7200 sec	160 - 180 °F @Time 2.00 hour

Descriptive Properties	Value	Comments
Appearance	Natural Color
Features	Electrically Conductive
	Good Wear Resistance
	High Stiffness
	Lubricated
Forms	Pellets
Generic Name	Polyamide 12 (Nylon 12)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Appliance Components
	Automotive Applications
	Bearings
	Business Equipment
	Consumer Applications
	Conveyor Parts
	Gears
	Industrial Applications
	Printer Parts
	Pulleys
	Rollers