Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.90 - 11.7 GPa | 420 - 1700 ksi | Average value: 9.21 GPa Grade Count:5 |
Overview of materials for Polyphthalamide (PPA), Stainless Fiber, EMI This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Stainless Fiber, EMI". Each property range of values reported is minimum and maximum va.. |
|||
Flexural Modulus | 3.44 - 11.7 GPa | 499 - 1700 ksi | Average value: 6.04 GPa Grade Count:23 |
Overview of materials for Polystyrene, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Glass Filled". Each property range of values reported is minimum and maximum values of appr.. |
|||
Flexural Modulus | 3.38 - 11.7 GPa | 490 - 1700 ksi | Average value: 5.50 GPa Grade Count:4 |
Overview of materials for Polyphenylene Ether, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Mineral Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Flexural Modulus | 5.66 - 11.7 GPa | 821 - 1700 ksi | Average value: 7.58 GPa Grade Count:4 |
Overview of materials for Polyamide-Imide, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Glass Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Flexural Modulus | 0.965 - 11.7 GPa | 140 - 1700 ksi | Average value: 4.13 GPa Grade Count:61 |
Overview of materials for High Density Polyethylene (HDPE), Glass fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Glass fiber Filled". Each property range of values reported is minimum.. |
|||
Flexural Modulus | 8.07 - 11.7 GPa | 1170 - 1700 ksi | Average value: 10.2 GPa Grade Count:3 |
Overview of materials for Phenolic, Graphite Cloth Composite This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Graphite Cloth Composite". Each property range of values reported is minimum and maximum value.. |
|||
Flexural Modulus | 2.10 - 11.7 GPa | 305 - 1700 ksi | Average value: 6.03 GPa Grade Count:78 |
Overview of materials for Nylon 6, Glass Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Filled, Impact Grade". Each property range of values reported is minimum and maximum valu.. |
|||
Flexural Modulus | 3.10 - 11.7 GPa | 450 - 1700 ksi | Average value: 7.93 GPa Grade Count:4 |
Overview of materials for Nylon 12, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
Flexural Modulus | 11.0 - 11.7 GPa | 1600 - 1700 ksi | ASTM D790 |
Mar-Bal MB1000-25 Thermoset Polyester Composite Molding Compound A general purpose material that is easily customized. Designed for Powder Coating and Electrostatic painting.Mar-Bal standard grades can be injection, compression and transfer molded.Information pro.. |
|||
Flexural Modulus | 11.0 - 11.7 GPa | 1600 - 1700 ksi | ASTM D790 |
Mar-Bal MB2000-25 Thermoset Polyester Composite Molding Compound An excellent flame and track resistant material with excellent electrical and mechanical properties. Good dielectric strength and low shrink for close dimensional control.Mar-Bal standard grades can.. |
|||
Flexural Modulus | 10.3 - 11.7 GPa | 1500 - 1700 ksi | |
Bulk Molding Compounds BMC T12-17394 General Purpose Molding Compound BMC T12-17394 is a general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC T12 is well suited for injection, transfer or compression molding of intricate parts. .. |
|||
Flexural Modulus | 10.3 - 11.7 GPa | 1500 - 1700 ksi | |
Bulk Molding Compounds BMC T12(18) General Purpose Molding Compound BMC T12(18) is a general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC T12 is well suited for injection, transfer or compression molding of intricate parts. Ty.. |
|||
Flexural Modulus | 7.00 - 11.7 GPa | 1020 - 1700 ksi | Average value: 9.72 GPa Grade Count:39 |
Overview of materials for Polycarbonate, 40% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Flexural Modulus | 6.90 - 11.7 GPa | 1000 - 1700 ksi | Average value: 10.3 GPa Grade Count:8 |
Overview of materials for Diallyl Phthalate (DAP), Cast, Mineral Filler This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP), Cast, Mineral Filler". Each property range of values reported is minimum and ma.. |
|||
Flexural Modulus | 3.40 - 11.7 GPa | 493 - 1700 ksi | Average value: 7.81 GPa Grade Count:22 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled". Each property range of values reported is .. |
|||
Flexural Modulus | 10.3 - 11.7 GPa | 1500 - 1700 ksi | |
Bulk Molding Compounds BMC T15(GPT) General Purpose Molding Compound BMC T15(GPT) is a high strength, low shrink general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC T15(GPT) is well suited for injection, transfer or compression.. |